BASF Ultramid® 8202C HS PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8202C HS PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in pigmented versions.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ISO 1183
Water Absorption	1.6 %	1.6 %	24 hour; ISO Test
	9.3 %	9.3 %	ISO 62
Moisture Absorption at Equilibrium	2.6 %	2.6 %	23°C/50% R.H.; ISO 62
Relative Viscosity	2.6 cP	2.6 cP	ISO Test; 96 % SAV
Viscosity Measurement	48	48	Formic Acid
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM Test
Tensile Strength at Break	90.0 MPa	13100 psi	0.2 in/min; ASTM Test
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ASTM Test
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ISO Data
	35.0 MPa @Temperature 80.0 °C	5080 psi @Temperature 176 °F	ISO Data
	35.0 MPa @Temperature 80.0 °C	5080 psi @Temperature 176 °F	ASTM Test
	130 MPa @Temperature -40.0 °C	18900 psi @Temperature -40.0 °F	ASTM Test
	130 MPa @Temperature -40.0 °C	18900 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Yield	88.0 MPa	12800 psi	50mm/min; ISO 527
	90.0 MPa	13100 psi	2 in/min; ASTM Test
	30.0 MPa @Temperature 120 °C	4350 psi @Temperature 248 °F	ASTM Test
	30.0 MPa @Temperature 120 °C	4350 psi @Temperature 248 °F	ISO Data
	40.0 MPa @Temperature 80.0 °C	5800 psi @Temperature 176 °F	ISO Data
	40.0 MPa @Temperature 80.0 °C	5800 psi @Temperature 176 °F	ASTM Test
	137 MPa @Temperature -40.0 °C	19900 psi @Temperature -40.0 °F	ASTM Test
	137 MPa @Temperature -40.0 °C	19900 psi @Temperature -40.0 °F	ISO Data
Elongation at Break	7.0 %	7.0 %	50mm/min, Nominal strain; ISO 527
	12 %	12 %	2 in/min; ASTM Test
	>= 100 %	>= 100 %
	5.0 % @Temperature -40.0 °C	5.0 % @Temperature -40.0 °F	ASTM Test
	5.0 % @Temperature -40.0 °C	5.0 % @Temperature -40.0 °F	ISO Data
	>= 100 % @Temperature 120 °C	>= 100 % @Temperature 248 °F	ISO Data
	>= 100 % @Temperature 80.0 °C	>= 100 % @Temperature 176 °F	ISO Data
	>= 100 % @Temperature 120 °C	>= 100 % @Temperature 248 °F	ASTM Test
Elongation at Yield	4.0 %	4.0 %	50mm/min; ISO 527
	4.0 %	4.0 %	2 in/min; ASTM Test
	3.0 % @Temperature -40.0 °C	3.0 % @Temperature -40.0 °F	ASTM Test
	3.0 % @Temperature -40.0 °C	3.0 % @Temperature -40.0 °F	ISO Data
	25 % @Temperature 80.0 °C	25 % @Temperature 176 °F	ASTM Test
	25 % @Temperature 80.0 °C	25 % @Temperature 176 °F	ISO Data
	27 % @Temperature 120 °C	27 % @Temperature 248 °F	ASTM Test
	27 % @Temperature 120 °C	27 % @Temperature 248 °F	ISO Data
Tensile Modulus	3.70 GPa	537 ksi	1mm/min; ISO 527
	0.550 GPa @Temperature 120 °C	79.8 ksi @Temperature 248 °F	ISO Data
	0.750 GPa @Temperature 80.0 °C	109 ksi @Temperature 176 °F	ISO Data
	4.09 GPa @Temperature -40.0 °C	593 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	95.0 MPa	13800 psi	ISO Data
	110 MPa	16000 psi	ASTM Test
	21.0 MPa @Temperature 120 °C	3050 psi @Temperature 248 °F	ASTM Test
	30.0 MPa @Temperature 65.0 °C	4350 psi @Temperature 149 °F	ASTM Test
	183 MPa @Temperature -40.0 °C	26500 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	2.80 GPa	406 ksi	ISO Data
	3.17 GPa	460 ksi	ASTM Test
	0.385 GPa @Temperature 120 °C	55.8 ksi @Temperature 248 °F	ASTM Test
	0.440 GPa @Temperature 93.0 °C	63.8 ksi @Temperature 199 °F	ASTM Test
	0.600 GPa @Temperature 65.0 °C	87.0 ksi @Temperature 149 °F	ASTM Test
Izod Impact, Notched	0.320 J/cm @Temperature -40.0 °C	0.599 ft-lb/in @Temperature -40.0 °F	ASTM Test
	0.480 J/cm @Thickness 3.17 mm	0.899 ft-lb/in @Thickness 0.125 in	ASTM Test
Charpy Impact Unnotched	NB	NB	ISO 179
Charpy Impact, Notched	0.350 J/cm²	1.67 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	81.0 µm/m-°C @Temperature -30.0 - 30.0 °C	45.0 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	165 °C	329 °F	ISO 75
	190 °C	374 °F	ASTM Test
Deflection Temperature at 1.8 MPa (264 psi)	65.0 °C	149 °F	ISO 75
	75.0 °C	167 °F	ASTM Test
Flammability, UL94	V-2 @Thickness 0.700 mm	V-2 @Thickness 0.0276 in
	V-2 @Thickness 3.00 mm	V-2 @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Comparative Tracking Index	600 V	600 V	IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	260 °C	500 °F	Injection molding
Mold Temperature	80.0 °C	176 °F	Injection molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Heat stabilized or stable to heat
UL.UL-C	Yes