Aclo Accutech Polypropylene Copolymer CP0437M10CL Mica Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437M10CL Mica Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 19 g/10 min | 19 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 53 | 53 | ASTM D785 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ASTM D638 |
| Elongation at Break | 17 % | 17 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.20 GPa | 174 ksi | ASTM D638 |
| Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 |
| Izod Impact, Notched | 2.51 J/cm | 4.70 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.2 °C | 189 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.1 °C | 124 °F |
Users viewing this material also viewed the following:
- DSM Arnite® TV4 460 KL TV4 460 PBT/PET Blend-30% Glass Reinforced (European Grade) (discontinued **)
- Huntsman IROGRAN® A 95 K 4640 TPU-For Seals
- Lubriplate GR-132 Portable Tool Grease Specialty Lubricant and Grease
- Solvay Specialty Polymers Hylar® Latex 932 Polyvinylidene Fluoride (PVDF)
- Dow Corning MOLYKOTE® 1122 CHAIN AND OPEN GEAR GREASE
- Covestro Baydur® SFR-243 Polyurethane Composite RRIM Foam, MDI-based 2-Component Liquid System
- Daikin NEOFLON AP-211SH PFA Semiconductor Grade
- E-Polymers TEKAMID® TA210IR Impact Modified PA66 Resin
- Arlon 56946C026 Silicone Rubber/Fiberglass Laminate
Copyright © lookpolymers.com All Rights Reserved