SABIC M40053S High Density Polyethylene for Injection Molding

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer	SABIC
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC M40053S High Density Polyethylene for Injection Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: M40053S is a UV stabilized high density polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to provide a good balance of stiffness and impact at low temperatures and also possesses good weatherability and surface properties. Typical Applications: M40053S is specially developed for the highly demanding dust bin market, shipped containers for low temperature storage, industrial pails, etc.Information provided by SABIC.

Physical Properties	Metric	English	Comments
Density	0.953 g/cc	0.0344 lb/in³	ASTM D1505
ESCR 100% Igepal®	7.0 hour	7.0 hour	F50; ASTM D1693B
ESCR 10% Igepal®	4.0 hour	4.0 hour	F50; ASTM D1693B
Melt Flow	4.0 g/10 min @Load 2.16 kg, Temperature 190 °C	4.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	60	60	ASTM D2240
Tensile Strength at Break	21.0 MPa	3050 psi	ASTM D638
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D638
Elongation at Break	>= 800 %	>= 800 %	ASTM D638
Flexural Strength	21.0 MPa	3050 psi	ASTM D790
Flexural Modulus	0.800 GPa	116 ksi	ASTM D790
1% Secant Modulus	900 MPa	131000 psi	ASTM D638
Izod Impact, Notched	1.50 J/cm	2.81 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Vicat Softening Point	125 °C	257 °F	ASTM D1525
Brittleness Temperature	<= -75.0 °C	<= -103 °F	ASTM D746

Processing Properties	Metric	English	Comments
Mold Temperature	15.0 - 60.0 °C	59.0 - 140 °F
Injection Pressure	60.0 - 100 MPa	8700 - 14500 psi