Borealis EE002AE Polypropylene Elastomer Modified

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer Borealis
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis EE002AE Polypropylene Elastomer Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EE002AE is a reactor elastomer modified polypropylene compound intended for injection molding. The product is available in natural color. This material has excellent balanced mechanical properties and gives a good surface quality. Applications: automotive exterior applications including bumpers and exterior trims.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0015 cm/cm
0.0015 in/in
post shrinkage (2h/90°C)
0.014 cm/cm
0.014 in/in
mold average
Melt Flow 11 g/10 min

@Load 2.16 kg,
Temperature 230 °C
11 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 55
55
ISO 868
Ball Indentation Hardness 36.0 MPa
5220 psi
132N/10s; ISO 2039
Tensile Strength, Yield 19.0 MPa
2760 psi
50mm/min; ISO 527-2
Elongation at Break >= 150 %
>= 150 %
50mm/min; ISO 527-2
Elongation at Yield 5.5 %
5.5 %
50mm/min; ISO 527-2
Tensile Modulus 0.950 GPa
138 ksi
1mm/min; ISO 527-2
Flexural Strength 21.0 MPa
3050 psi
ISO 178
Flexural Modulus 0.900 GPa
131 ksi
2mm/min; ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature -20.0 °C
5.71 ft-lb/in²

@Temperature -4.00 °F
ISO 180/1A
57.0 kJ/m²

@Temperature 23.0 °C
27.1 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.850 J/cm²

@Temperature -20.0 °C
4.04 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
7.00 J/cm²

@Temperature 23.0 °C
33.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 100 µm/m-°C

@Temperature -30.0 - 80.0 °C
55.6 µin/in-°F

@Temperature -22.0 - 176 °F
Borealis Method
Deflection Temperature at 0.46 MPa (66 psi) 75.0 °C
167 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C
118 °F
ISO 75-2
Vicat Softening Point 45.0 °C

@Load 5.10 kg
113 °F

@Load 11.2 lb
ISO 306
135 °C

@Load 1.02 kg
275 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 - 260 °C
428 - 500 °F
mass temperature
Feed Temperature 40.0 - 80.0 °C
104 - 176 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec
3.94 - 7.87 in/sec
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Descriptive Properties Value Comments
Back Pressure low to medium
Screw Speed low to medium