SABIC Innovative Plastics LNP THERMOCOMP TH0815A
| Category | Polymer , Thermoplastic |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP TH0815A.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* TH0815A is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.15 g/cc | 0.294 lb/in³ | ASTM D792 |
| 8.15 g/cc | 0.294 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0048 cm/cm @Time 86400 sec |
0.0048 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0049 cm/cm @Time 86400 sec |
0.0049 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| 17.0 MPa | 2470 psi | ISO 527 | |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
| 19.0 MPa | 2760 psi | ISO 527 | |
| Elongation at Break | 25.4 % | 25.4 % | ASTM D638 |
| 26.5 % | 26.5 % | ISO 527 | |
| Elongation at Yield | 13.2 % | 13.2 % | ASTM D638 |
| 13.7 % | 13.7 % | ISO 527 | |
| Tensile Modulus | 1.12 GPa | 162 ksi | 1 mm/min; ISO 527 |
| 1.33 GPa | 193 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 20.0 MPa | 2900 psi | ASTM D790 |
| 21.0 MPa | 3050 psi | ISO 178 | |
| Flexural Modulus | 1.39 GPa | 202 ksi | ISO 178 |
| 1.52 GPa | 220 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.44 J/cm | 2.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.57 J/cm | 19.80 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 73.0 kJ/m² | 34.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J | 11.8 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 12.0 J | 8.85 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 86.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
48.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 87.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
48.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 72.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 42.0 °C @Thickness 3.20 mm |
108 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B1 GF 15 FRX 5 PBT reinforced with 15% glass fibre, with flame retardant
- Network Polymers NPP 20-0202
- Solvay IGEPAL® CA 520 Surfactant
- Wellman Wellamid® NY1599-GY Unfilled Nylon 66
- Total HDPE XT10B High Density Polyethylene, Pipe Resin
- A. Schulman PAPERMATCH® T-4228-50 Specialty Masterbatch
- Eagle Brass 519 Phosphor Bronzes 6%, Spring
- ChevronTexaco Vistac® ISO 68 Way Oil
- BACT Dylyn® Diamond-Like Nanocomposite Coating
- BASF Triisopropanolamine 85% Solution
Copyright © lookpolymers.com All Rights Reserved