UBE UBESTA® 3030JI6L Plasticized Automotive Grade Nylon 12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | UBE |
| Trade Name | UBESTA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBESTA® 3030JI6L Plasticized Automotive Grade Nylon 12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBE UBESTA® Automotive grade Nylon 12Comments: for multilayer tubeInformation provided by UBE.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ASTM D792 |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 235 °C |
0.50 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength at Break | >= 56.0 MPa | >= 8120 psi | ASTM D638 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | >= 300 % | >= 300 % | ASTM D638 |
| Flexural Strength | 21.0 MPa | 3050 psi | ASTM D790 |
| Flexural Modulus | 0.480 GPa | 69.6 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 175 °C | 347 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C | 259 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 230 °C | 446 °F | Flange Temperature for T-Die Cast Film Extrusion |
| Feed Temperature | 40.0 °C | 104 °F | Injection Molding |
| Zone 1 | 190 °C | 374 °F | For T-Die Cast Film Extrusion |
| 230 °C | 446 °F | For 8x1 mm Tube Extrusion | |
| Zone 2 | 210 °C | 410 °F | For T-Die Cast Film Extrusion |
| 225 °C | 437 °F | For 8x1 mm Tube Extrusion | |
| Zone 3 | 220 °C | 428 °F | For 8x1 mm Tube Extrusion |
| 230 °C | 446 °F | For T-Die Cast Film Extrusion | |
| Zone 4 | 215 °C | 419 °F | For 8x1 mm Tube Extrusion |
| Die Temperature | 230 °C | 446 °F | For T-Die Cast Film Extrusion |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Injection Velocity | 100 mm/sec | 3.94 in/sec | Injection Molding |
| Die Opening | 0.0400 cm | 0.0157 in | For T-Die Cast Film Extrusion |
| Roll Temperature | 50.0 °C | 122 °F | Chill Roll Temperature for T-Die Cast Film Extrusion |
| Drying Temperature | 80.0 °C | 176 °F | Option 1 |
| 100 °C | 212 °F | Option 2 | |
| 110 °C | 230 °F | Option 3 | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Option 3 |
| 4 - 6 hour | 4 - 6 hour | Option 2 | |
| 6 - 8 hour | 6 - 8 hour | Option 1 | |
| Injection Pressure | 40.0 - 50.0 MPa | 5800 - 7250 psi | Injection Molding (Injection pressure should be increased when molding thin wall parts. Pressure up to 75 bar can be used here.) |
| Hold Pressure | 25.0 - 50.0 MPa | 3630 - 7250 psi | Injection Molding |
| Back Pressure | 5.00 MPa | 725 psi | Injection Molding |
| Screw Speed | 15 - 76 rpm | 15 - 76 rpm | For 8x1 mm Tube Extrusion |
| Descriptive Properties | Value | Comments |
|---|---|---|
| C/R | 3-3.5:1 | For 8x1 mm Tube Extrusion |
| Calibrating Vacuum | 100 mbar | For 8x1 mm Tube Extrusion |
| Calibration | 9.95 mm | For 8x1 mm Tube Extrusion |
| Compression Ratio | 2.5-3.5:1 | Injection Molding |
| min 3:1 | For 8x1 mm Tube Extrusion | |
| Die Diameter | 16 mm | For 8x1 mm Tube Extrusion |
| Die Width | 300 mm | For T-Die Cast Film Extrusion |
| Extractables | 7% | Tolerance (DIN 73378 EtOH 18hr) 2% |
| Extruder | Barmag, Screw Diameter = 30 mm | For T-Die Cast Film Extrusion |
| Extruder Characteristics | 65 mm screw diameter | For 8x1 mm Tube Extrusion |
| Film Thickness | 60 microns | For T-Die Cast Film Extrusion |
| Flight Depth in the Feeding Zone | 10-15% of Screw Diameter | Injection Molding |
| Flight Depth in the Metering Zone | 5-7% of Screw Diameter | Injection Molding |
| Haul Off Speed | 5 m/min | For T-Die Cast Film Extrusion |
| Haul Speed | 10-55 m/min | For 8x1 mm Tube Extrusion |
| L/D Ratio | 25:1 | For 8x1 mm Tube Extrusion |
| min 20:1 | Injection Molding | |
| Length of Compression Zone | 25-45% of total screw length | Injection Molding |
| 30% of screw length | For 8x1 mm Tube Extrusion | |
| Length of Feeding Zone | 20-40% of total screw length | Injection Molding |
| 30-40% of screw length | For 8x1 mm Tube Extrusion | |
| Length of Metering Zone | 30-45% of screw length | For 8x1 mm Tube Extrusion |
| 35-45% of total screw length | Injection Molding | |
| Mandrel Diameter | 12 mm | For 8x1 mm Tube Extrusion |
| Peripheral screw speed | 10 m/min | Injection Molding |
| Water Temperature | 10-18°C | For 8x1 mm Tube Extrusion |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 75 HID General Purpose Acrylic Resin
- SABIC Innovative Plastics Lexan® EXL1182T PC Copolymer (Europe-Africa-Middle East)
- Saint-Gobain CHR® SG03-14(R) Premium Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- Silon TA 2322 HD Blue Catalyst Masterbatch
- Fainplast Compounds HAX HFX 024-15C Halogen Free PVC
- Fainplast Compounds HAX HF 4221 Halogen Free PVC
- Dynasol Solprene® 411 Thermoplastic Rubber SBS Dry
- Carmel Olefins CAPILENE® T 12 EV Polypropylene Homopolymer
- BASF Elastollan® S85A Polyester Type Polyurethane Elastomer
- Buckeye Polymers BP RPP 2006 T Polypropylene, 20% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved