Borealis Daplen™ EF005AE Polypropylene TPO Compound

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Mica Filler , Polypropylene, Mineral Reinforced
Manufacturer	Borealis
Trade Name	Daplen™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis Daplen™ EF005AE Polypropylene TPO Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Daplen™ EF005AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, gives a good surface quality and is easy to process. Applications: Daplen™ EF005AE has been developed especially for the car industry to be used in automotive exterior parts including bumpers, exterior trims, and spoilers.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	0.950 g/cc	0.0343 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0015 cm/cm	0.0015 in/in	post shrinkage; 2 hours, 90°C
	0.0080 cm/cm	0.0080 in/in	mold average;Borealis Method
Melt Flow	25 g/10 min @Load 2.16 kg, Temperature 230 °C	25 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	23.0 MPa	3340 psi	132 N/10s; ISO 2039
Tensile Strength, Yield	16.0 MPa	2320 psi	50mm/min; ISO 527-2
Elongation at Break	80 %	80 %	50mm/min; ISO 527-2
Elongation at Yield	7.0 %	7.0 %	50mm/min; ISO 527-2
Tensile Modulus	1.06 GPa	154 ksi	1mm/min; ISO 527-2
Flexural Strength	21.0 MPa	3050 psi	ISO 178
Flexural Modulus	1.07 GPa	155 ksi	2mm/min; ISO 178
Izod Impact, Notched (ISO)	4.50 kJ/m² @Temperature -20.0 °C	2.14 ft-lb/in² @Temperature -4.00 °F	ISO 180/1A
	40.0 kJ/m² @Temperature 23.0 °C	19.0 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
	NB @Temperature -20.0 °C	NB @Temperature -4.00 °F	ISO 179/1eU
Charpy Impact, Notched	0.400 J/cm² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.600 J/cm² @Temperature -20.0 °C	2.86 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eA
	5.20 J/cm² @Temperature 23.0 °C	24.7 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear	65.0 µm/m-°C @Temperature -30.0 - 80.0 °C	36.1 µin/in-°F @Temperature -22.0 - 176 °F	Borealis Method
Deflection Temperature at 0.46 MPa (66 psi)	85.0 °C	185 °F	ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi)	49.0 °C	120 °F	ISO 75-2
Vicat Softening Point	39.0 °C @Load 5.10 kg	102 °F @Load 11.2 lb	ISO 306
	121 °C @Load 1.02 kg	250 °F @Load 2.25 lb	ISO 306

Processing Properties	Metric	English	Comments
Processing Temperature	220 - 260 °C	428 - 500 °F	mass temperature
Feed Temperature	40.0 - 80.0 °C	104 - 176 °F
Mold Temperature	30.0 - 50.0 °C	86.0 - 122 °F
Injection Velocity	100 - 200 mm/sec	3.94 - 7.87 in/sec
Hold Pressure	30.0 - 60.0 MPa	4350 - 8700 psi

Descriptive Properties	Value	Comments
Back Pressure	low to medium
Screw Speed	low to medium