Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Murtfeldt Murinit® SP Polyphenylene Sulfide Thanks to the low fiber content and integrated solid lubricant, Murinit® SP offers an excellent combination of good slide and wear behavior, high strength, and dimensional stability – even at high.. |
|||
Modulus of Elasticity | 4.00 - 6.00 GPa | 580 - 870 ksi | Compression; ISO 527 |
Raschig Group 6551 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
Modulus of Elasticity | 4.00 - 6.00 GPa | 580 - 870 ksi | Compression; ISO 527 |
Raschig Group RALUPOL® 2100 UP Polyester Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta.. |
|||
Modulus of Elasticity | 4.00 - 10.8 GPa | 580 - 1560 ksi | Average value: 7.53 GPa Grade Count:27 |
Overview of materials for PBT + ASA Blend, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PBT + ASA Blend, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum .. |
|||
Modulus of Elasticity | 4.00 - 37.2 GPa | 580 - 5400 ksi | Average value: 15.3 GPa Grade Count:47 |
Overview of materials for Nylon 6, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of a.. |
|||
Modulus of Elasticity | 4.00 - 15.8 GPa | 580 - 2290 ksi | Average value: 7.01 GPa Grade Count:36 |
Overview of materials for Nylon 12, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-8052/EM/BL PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-8135/GN PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-8135/VI PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-8174 PEEK, with PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 20-7796 Polyphthalamide, with aramid reinforcement and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low influence from moisture an.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 50/GF/10/TF/18/SI/2/GY5 Polycarbonate, with glass fiber, PTFE, lubricant modified Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 50-7224/V0 Polycarbonate, with glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Reduced moment of inertia compared with metal parts.Improved f.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 80-8387 Polyacetal-copolymer, unreinforced Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Isotropic shrinkage characteristics.Strong, stiff parts.Impact resistance.Control disks, cams, .. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 80-8387/EM Polyacetal-copolymer, unreinforced Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Isotropic shrinkage characteristics.Strong, stiff parts.Impact resistance.Control disks, cams, .. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | Storage |
Lord Adhesives Thermosetâ„¢ ME-525 Underfill Encapsulant LORD Thermosetâ„¢ ME-525 encapsulant is a high purity, semiconductor grade epoxy underfill product developed for the encapsulation of flip chip devices. It is formulated to reduce warpage and wit.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-0856/GY7 PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-7596/BL PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-7714 PEEK, with PTFE, lubricant modified, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1105-7740 PEEK, lubricant modified, heat stabilized Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1-7984 Polyamide 66, with aramid reinforcement and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Emergency running property.Improved heat resistance.Control disks, cams, sliding elements and o.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 21MB621 OPP Film Product Description: Biaxially oriented transparent polypropylene film with heat sealable coating applied to both sides. The static resistant feature of this film prevents the attraction of dust, an.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 26MB600 OPP Film Product Description: Biaxially oriented transparent polypropylene film, acrylic coated two sides. Gives outstanding performance on overwrap and HFFS machines.Availability: Africa & Middle East, Asia.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | ISO 178 |
Addiplast Addilene H 242 M40 Polypropylene Homopolymer High heat resistance, detergent stabilizedInformation provided by Addiplast. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | ISO 527-2 |
BASF Ultradur® S 4090 GM11 5/5% Glass/Mineral Filled PBT Description: Is a PBT + ASA, injection-molding grades reinforced with 5% glass fiber/mineral, for laminar parts with high demands on dimensional stability and low warpage, e.g. lids, ventilation gri.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | ISO 527-2 |
BASF Ultraform® N2720 M210 POM Description: Is a POM, product with increased stiffness and strength as well as good wear characteristics, used, for instance, for sliding chains and conveyor systems.Information provided by BASF |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | Conditioned; ISO 178 |
Addiplast Addinyl A2H M30 Flame Retardant Nylon 66, 30% Mineral Filled Flame retardant, 30% mineral filled, with halogensInformation provided by Addiplast. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | ISO 527-2 |
BASF Ultradur® B 4300 K6 30% Glass Bead Filled PBT Description: Is a PBT + ASA, Injection-molding grades containing 30% of glass beads for industrial parts with low warpage.Applications: Precision parts for optical instruments, fuel tank sensor unit.. |
|||
Modulus of Elasticity | 4.00 GPa | 580 ksi | |
Lehmann & Voss LUVOCOM® 1-8228 Polyamide 66, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |