Lehmann & Voss LUVOCOM® 1-7984 Polyamide 66, with aramid reinforcement and PTFE, heat stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Aramid Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1-7984 Polyamide 66, with aramid reinforcement and PTFE, heat stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Emergency running property.Improved heat resistance.Control disks, cams, sliding elements and other duty parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0080 - 0.014 cm/cm | 0.0080 - 0.014 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 80.0 MPa | 11600 psi | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| 6.5 % | 6.5 % | flexural | |
| Modulus of Elasticity | 4.00 GPa | 580 ksi | |
| Flexural Strength | 115 MPa | 16700 psi | |
| Flexural Modulus | 3.00 GPa | 435 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.13 | 0.13 | |
| Coefficient of Friction, Static | 0.12 | 0.12 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| 160 °C | 320 °F | short term | |
| Vicat Softening Point | 260 °C | 500 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | yellow |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® IP1000 PC+ABS
- SABIC Innovative Plastics Lexan® OQ4320 PC (Europe-Africa-Middle East)
- PolyOne Lubri-Tech™ AS-000/10T-2S ABS - 10% PTFE - 2% Silicone (discontinued **)
- Solvay TECHNYL® A 218 V43 Black 21 N PA66, 43% glass fiber, DRY
- Silberline Dedusted Flake Series DF-3622 Aluminum Flake
- Sumitomo Bakelite Durez® 152 Phenolic, Injection Grade
- Zeon Chemicals Zetpol® ZCS 2295CX Hydrogenated Nitrile Elastomomer
- A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene
- Arkema Group Lucalor® RB 1167 CPVC, Pipe Grade
- BASF Lupranate® 233 Isocyanate
Copyright © lookpolymers.com All Rights Reserved