Lehmann & Voss LUVOCOM® 1105-8135/VI PEEK, unreinforced, easy flowing
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-8135/VI PEEK, unreinforced, easy flowing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical resistance parts, non flammable.Inherent flame resistance.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | 23°C/24h |
| Linear Mold Shrinkage | 0.010 - 0.016 cm/cm | 0.010 - 0.016 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 100 MPa | 14500 psi | |
| Elongation at Yield | 4.5 % | 4.5 % | |
| 6.0 % | 6.0 % | flexural | |
| Modulus of Elasticity | 4.00 GPa | 580 ksi | |
| Flexural Strength | 140 MPa | 20300 psi | |
| Flexural Modulus | 3.00 GPa | 435 ksi | |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 260 °C | 500 °F | short term | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | dark violet |
Users viewing this material also viewed the following:
- Polymer Resources NY6-GP1 General Purpose Nylon 6
- SABIC Innovative Plastics Lexan® HPS2R PC (Europe-Africa-Middle East)
- ExxonMobil LD 117.03 Blown Overwrap Film Resin (discontinued **)
- Lucent Polymers PC-1406 Polycarbonate, Extrusion/Blow Molding Grade
- Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours
- Shin-Etsu Silicones KSG-43 Fluid
- Toyobo VYLOPET® EMC133 Injection Molding Polyester Resin, Hydrolysis Resistant
- BASF Neopor® 2300 Expandable Polystyrene
- Axiall 10702 Wire & Cable Flexible PVC
- CeramTec Sonox® P4 Piezoceramic
Copyright © lookpolymers.com All Rights Reserved