POLYMER SEARCH

ExxonMobil Bicor™ 21MB621 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Bicor™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Bicor™ 21MB621 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Biaxially oriented transparent polypropylene film with heat sealable coating applied to both sides. The static resistant feature of this film prevents the attraction of dust, and contributes to excellent machine performance even on critical packaging machines. The acrylic coating is water based and provides wide heat sealing range on packaging equipment.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Low sealing thresholdEfficient Sealability under Low PressureOptimum and Stable Coefficient of FrictionExcellent Performance on Overwrap Packaging MachinesOutstanding Optical PropertiesGood Aroma BarrierIdeal Support for Normal Ink SystemsWater Based CoatingsFeatures:Acrylic CoatedFlavor & Aroma Barrier Applications: Box OverwrapConfectionery, Chocolate Confectionery, Gum Confectionery, SugarHealth and Beauty Care Uses: Box Overwrap Flexible Packaging Processing Method: Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	1.40 g/m²/day @Temperature 23.0 °C	0.0900 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	6.98 g/m²/day @Temperature 38.0 °C	0.450 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Thickness	21.1 microns	0.830 mil	ExxonMobil Method
Coating Weight	18.7 g/m²	11.7 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	140 %	140 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	50 %	50 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	2.20 GPa	319 ksi	MD; ExxonMobil Method
	4.00 GPa	580 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	Both Sides; ExxonMobil Method
Seal Strength	200 g/25 mm @Pressure 0.00345 MPa, Temperature 100 °C	200 g/in @Pressure 0.500 psi, Temperature 212 °F	0.5 sec, LPS; ExxonMobl Method
	510 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C	510 g/in @Pressure 40.0 psi, Temperature 284 °F	Otto Bruger, 0.2 sec; ExxonMobl Method
Film Tensile Strength at Break, MD	130 MPa	18900 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	250 MPa	36300 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	5.0 % @Temperature 135 °C, Time 432 sec	5.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	3.0 % @Temperature 135 °C, Time 432 sec	3.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	1.0 %	1.0 %	ExxonMobil Method
Gloss	85 %	85 %	45°; ExxonMobil Method

Descriptive Properties	Value	Comments
Heat Seal Range	72°F	36.3 psi, 0.2 sec
Yield	36800 in²/lb