Addiplast Addinyl A2H M30 Flame Retardant Nylon 66, 30% Mineral Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled |
| Manufacturer | Addiplast |
| Trade Name | Addinyl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addinyl A2H M30 Flame Retardant Nylon 66, 30% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, 30% mineral filled, with halogensInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 81 | 81 | Conditioned; ISO 868 |
| 86 | 86 | ISO 868 | |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Conditioned; ISO R 527 |
| 72.0 MPa | 10400 psi | ISO R 527 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO R 527 |
| 8.0 % | 8.0 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 4.00 GPa | 580 ksi | Conditioned; ISO 178 |
| 7.50 GPa | 1090 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1A |
| 4.00 kJ/m² | 1.90 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179/IeU |
| 4.00 J/cm² | 19.0 ft-lb/in² | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/IeA |
| 0.400 J/cm² | 1.90 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-2/AF |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Oxygen Index | 32 % | 32 % | ISO 4589 |
| Glow Wire Test | 960 °C | 1760 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | CEI 60093 |
| Comparative Tracking Index | 300 V | 300 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N1233HL BK Nylon 6/6
- Karina E TR-600N35/1-YT-A Ivory TR (SP31503)
- Solvay Technyl® C 216 Nylon 6, 30% Glass Fiber, EH0
- SGL Carbon Group EK 3245 Carbon Graphite
- Teknor Apex Chemlon® 223 Nylon 6, Unreinforced
- DuPont Vamac® DP Test Compound
- Polyram PlusTek PA303G5 Nylon 6.6, 25% Glass Fiber
- Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, 50% RH
- Ineos H12G-00 Polypropylene Homopolymer
- Bhansali Engineering Abstron MIF45EP ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved