ExxonMobil Bicor™ 26MB600 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Bicor™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Bicor™ 26MB600 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Biaxially oriented transparent polypropylene film, acrylic coated two sides. Gives outstanding performance on overwrap and HFFS machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Low sealing thresholdLow Sealing ThresholdEfficient Sealability under Low PressureGood Aroma BarrierOutstanding Optical PropertiesExcellent Performance on Overwrap Packaging MachinesIdeal Support for Normal Ink SystemsWater Based CoatingsFeatures:Acrylic CoatedFlavor & Aroma BarrierApplications:Biscuits/Cookie/CrackersBox OverwrapConfectionery, Chocolate Confectionery, Gum Confectionery, Sugar Health and Beauty Care Uses:Box Overwrap Flexible PackagingPre-made Bags – Flexible Packaging Processing Method: Inner Web Adhesive Lamination, Outer Web Adhesion, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	1.10 g/m²/day @Temperature 23.0 °C	0.0710 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	4.97 g/m²/day @Temperature 38.0 °C	0.320 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	850 cc/m²/day @Temperature 23.0 °C	54.8 cc/100 in²/day @Temperature 73.4 °F	Wet, 75% RH; ExxonMobil Method
	854 cc/m²/day @Temperature 23.0 °C	55.0 cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
Thickness	25.4 microns	1.00 mil	ExxonMobil Method
Coating Weight	23.4 g/m²	14.6 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	140 %	140 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	50 %	50 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	2.20 GPa	319 ksi	MD; ExxonMobil Method
	4.00 GPa	580 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	Both Sides; ExxonMobil Method
Seal Strength	200 g/25 mm @Pressure 0.00345 MPa, Temperature 100 °C	200 g/in @Pressure 0.500 psi, Temperature 212 °F	LSP, 0.5 sec; ExxonMobil Method
	510 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C	510 g/in @Pressure 40.0 psi, Temperature 266 °F	Otto Brugger, 0.2 sec; ExxonMobil Method
Film Tensile Strength at Break, MD	130 MPa	18900 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	250 MPa	36300 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	5.0 % @Temperature 135 °C, Time 432 sec	5.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	3.0 % @Temperature 135 °C, Time 432 sec	3.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	1.3 %	1.3 %	ExxonMobil Method
Gloss	86 %	86 %	45°; ExxonMobil Method

Descriptive Properties	Value	Comments
Heat Seal Range	90°F	36.3 psi, 0.2 sec
Yield	29700 in²/lb