Lehmann & Voss LUVOCOM® 80-8387 Polyacetal-copolymer, unreinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80-8387 Polyacetal-copolymer, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Isotropic shrinkage characteristics.Strong, stiff parts.Impact resistance.Control disks, cams, sliding elements and other duty parts.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.84 g/cc | 1.84 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.018 - 0.025 cm/cm | 0.018 - 0.025 in/in | |
| Melt Flow | 16.56 g/10 min @Load 2.16 kg, Temperature 190 °C |
16.56 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 54.0 MPa | 7830 psi | |
| Elongation at Yield | 4.5 % | 4.5 % | |
| 5.5 % | 5.5 % | flexural | |
| Modulus of Elasticity | 4.00 GPa | 580 ksi | |
| Flexural Strength | 79.0 MPa | 11500 psi | |
| Flexural Modulus | 3.50 GPa | 508 ksi | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term | |
| Flammability, UL94 | HB | HB | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+11 ohm | >= 1.00e+11 ohm | |
| Insulation Resistance | >= 1.00e+11 ohm | >= 1.00e+11 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- RheTech Products HP514-438 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 167 Ebony
- LATI LASTIROL R-V2 Polystyrene (PS) (UL94 V-2) (discontinued **)
- Techmer ES Elastoblend® PA6 GF43 IM L BKN 43% Glass Filled
- Styrolution Absolac® 120 HR ABS
- Styron DL 460NA SB Latex
- PlastxWorld CEVIAN® S3500 PC/ABS alloy
- A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Chosun Refractories SCX-60KL Special SiC Castable
- Clariant Renol SB83642580 ASA Polymer
- Colorite Polymers 8011G-015 (Extrustion), 8012G-015 (Molding) Radiation Sterilizable Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved