- Lehmann & Voss LUVOCOM® 1105-7740 PEEK, lubricant modified, heat stabilized
Lehmann & Voss LUVOCOM® 1105-7740 PEEK, lubricant modified, heat stabilized
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, PTFE-Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-7740 PEEK, lubricant modified, heat stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behaviour, self-lubricating, for highest tribologic needs.High dimensionally stable precision parts, high continuous use temperature.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0050 - 0.015 cm/cm | 0.0050 - 0.015 in/in | |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 380 °C |
20 g/10 min @Load 22.0 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 96.0 MPa | 13900 psi | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| 6.6 % | 6.6 % | flexural | |
| Modulus of Elasticity | 4.00 GPa | 580 ksi | |
| Flexural Strength | 140 MPa | 20300 psi | |
| Flexural Modulus | 3.40 GPa | 493 ksi | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 260 °C | 500 °F | short term | |
| Vicat Softening Point | 280 °C | 536 °F | DIN ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | dark grey |
Users viewing this material also viewed the following:
- Oceanchem Group Xanthan Gum Oil Drilling Grade
- SABIC Innovative Plastics SABIC PPCOMPOUND 37T1020 PP
- SABIC Innovative Plastics LNP STAT-KON AE003 ABS (Europe-Africa-Middle East)
- Samsung Cheil Industries Starex® HF-0660IW ABS, Unreinforced
- Lubrizol Estane® S398A Thermoplastic Polyurethane
- A. Schulman POLYBATCH™ Red LL50283/3 Concentrate Based In LLDPE
- Wanhua Chemical Wanthane® WHT-1495RV Polyester Based TPU
- A. Schulman SCHULAMID® 66 MK20HI 20% Mineral Reinforced, Impact Modified Nylon 66
- Asahi Kasei Thermylene® P-20-0739 20% Talc Filled, High Impact, Heat Stabilized
- 3M ScotchPad™ 832 Pouch Tape Pads
Copyright © lookpolymers.com All Rights Reserved