Lehmann & Voss LUVOCOM® 20-7796 Polyphthalamide, with aramid reinforcement and PTFE
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Aramid Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 20-7796 Polyphthalamide, with aramid reinforcement and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low influence from moisture and temperature to measures and electrical properties, compared with PA66Suitable for metall inserts.Bearings, sleeves, sliding elements, control disks, gear wheels, duty parts in switches.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0070 - 0.014 cm/cm | 0.0070 - 0.014 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 80.0 MPa | 11600 psi | |
| Elongation at Yield | 2.8 % | 2.8 % | |
| 3.8 % | 3.8 % | flexural | |
| Modulus of Elasticity | 4.00 GPa | 580 ksi | |
| Flexural Strength | 115 MPa | 16700 psi | |
| Flexural Modulus | 3.40 GPa | 493 ksi | |
| Charpy Impact Unnotched | 1.90 J/cm² | 9.04 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| 195 °C | 383 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 330 °C | 608 - 626 °F | |
| Zone 1 | 320 - 340 °C | 608 - 644 °F | |
| Zone 2 | 320 - 345 °C | 608 - 653 °F | |
| Zone 3 | 325 - 350 °C | 617 - 662 °F | |
| Mold Temperature | 135 - 160 °C | 275 - 320 °F | |
| Drying Temperature | 80.0 °C @Time 57600 sec |
176 °F @Time 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 18000 sec |
221 °F @Time 4.00 - 5.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (yellow) |
Users viewing this material also viewed the following:
- Huntsman Araldite GY 506 Bisphenol A Epoxy Liquid Resin
- Kureha KF Polymer 850 PVDF Homopolymer
- Shandong Rike Chemical HELIâ„¢ HL-530 PVC Foaming Regulator
- Samsung Cheil Industries Starex® BF-0930 MABS, Unreinforced Scratch Resistant
- SABIC Innovative Plastics NORYL N110S PPE+HIPS (Europe-Africa-Middle East)
- DSM Arnitel® PM381 Polyether Ester Elastomer (European Grade)
- Arkema Group Orgalloy® LE 60LMES Flexible Nylon Alloy (Conditioned)
- 3M FP08N Clear Polypropylene Label Products
- Ineos Nova Zylar® 530 Clear Impact Modified Acrylic Copolymer (discontinued **)
- Solvay RHODAFAC® RS-610 E Surfactant
Copyright © lookpolymers.com All Rights Reserved