LG Chemical LUCON PO6062 mPPO+CNT+CF+GF
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 10% Glass Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCON PO6062 mPPO+CNT+CF+GF.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, mPPO+CNT+CF+GF, High Strength, Heat StabilityApplication: ATM parts, LCD Cell TrayCAS No. 35134-01-4, 25038-54-4, 65997-17-3, 7440-44-0 and 7782-42-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 300 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 572 °F |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 167 MPa @Thickness 3.20 mm |
24200 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 8.0 % @Thickness 3.20 mm |
>= 8.0 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 235 MPa @Thickness 3.20 mm |
34100 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Flexural Modulus | 0.981 GPa @Thickness 3.20 mm |
142 ksi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.65 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C @Thickness 6.40 mm |
383 °F @Thickness 0.252 in |
ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 1.00e+6 ohm | 10000 - 1.00e+6 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding |
| Middle Barrel Temperature | 290 - 300 °C | 554 - 572 °F | Injection Molding |
| Front Barrel Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding |
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | Injection Molding |
| Drying Temperature | 90.0 - 110 °C | 194 - 230 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.000 - 1.96 MPa | 0.000 - 284 psi | Injection Molding |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate
- H.C. Starck Amperit® 515.2 Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12
- SSAB Tunnplat Docol® 600DP High-strength Steel
- Techmer ES Luriblend® POM CO GF20 TL15 20% Glass Filled
- Silberline Sparkle Silvex® Premier 950-20-D
- A. Schulman POLYBATCH™ Yellow 2057E Concentrate Based In Polyethylene
- EPICHEM Epilen PP 20GF NAT Polypropylene, 20% Glass Fiber
- ExxonMobil Santoprene® 271-73 Thermoplastic Elastomer
- Aclo Accutech Polypropylene Homopolymer HP0336G20CL Glass Reinforced Coupled
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 65A
Copyright © lookpolymers.com All Rights Reserved