SABIC Innovative Plastics LNP Thermocomp RF007ESS PA 66 (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Thermocomp RF007ESS PA 66 (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Thermocomp* RF007ESS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/inÂ³	ISO 1183
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	on tensile bar; SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	178 MPa	25800 psi	5 mm/min; ISO 527
Elongation at Break	2.4 %	2.4 %	5 mm/min; ISO 527
Flexural Strength	235 MPa	34100 psi	2 mm/min; ISO 178
Flexural Modulus	9.10 GPa	1320 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	10.0 kJ/mÂ² @Temperature 23.0 Â°C	4.76 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	50.0 kJ/mÂ² @Temperature 23.0 Â°C	23.8 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	237 Â°C	459 Â°F	Flatw 80104 sp=64mm; ISO 75/Af