SABIC Innovative Plastics LNP STAT-KON AE004 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON AE004 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* AE004 is a compound based on ABS resin containing 20% Carbon Fiber. Added feature of this material is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.250 % | 0.250 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
| 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 12.96 GPa | 1880 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 152 MPa | 22000 psi | ISO 178 | |
| Flexural Modulus | 10.61 GPa | 1539 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 12.75 GPa | 1849 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.20 J/cm | 5.99 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 71.5 µm/m-°C @Temperature -30.0 - 30.0 °C |
39.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- LyondellBasell Montell 16502F7 Butene LLDPE
- LyondellBasell Alathon® M6010SB High Density Polyethylene, MMW Film Grade
- Mateck Laser Grade Zinc Selenide, ZnSe CVD
- Lord Adhesives Circalokâ„¢ 6037 Epoxy Adhesive
- Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet
- SABIC Innovative Plastics ULTEM AR9300 PEI
- A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer
- EMS-Grivory Grivory® XE 4028 nat PA12/MACMI
- 3M Scotch® 864 Reinforced Strapping Tape
- C.O.I.M. PLAXTER® P 05 Low Viscosity Polymeric Plasticizer
Copyright © lookpolymers.com All Rights Reserved