SABIC Innovative Plastics LNP THERMOCOMP DX10311 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DX10311 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DX10311 is 30% glass fiber reinforced, impact modified polycarbonate resin. High flow and good ductility.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 37 g/10 min @Load 5.00 kg, Temperature 300 °C |
37 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5 mm/min; ASTM D638 |
| 119 MPa | 17300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 |
| 2.7 % | 2.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 8.26 GPa | 1200 ksi | 1 mm/min; ISO 527 |
| 8.33 GPa | 1210 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 181 MPa | 26300 psi | 2 mm/min; ISO 178 |
| 190 MPa | 27600 psi | ASTM D790 | |
| Flexural Yield Strength | 182 MPa | 26400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.67 GPa | 1110 ksi | ASTM D790 |
| 7.72 GPa | 1120 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.96 J/cm | 3.67 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.52 J/cm | 14.1 ft-lb/in | ASTM D4812 |
| Charpy Impact Unnotched | 5.70 J/cm² | 27.1 ft-lb/in² | ISO 179/2C |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics GELOY XP7560 ASA (Europe-Africa-Middle East)
- KaMin KaMin® Tek 2001 Clay
- Techmer ES HiFill® PA6 GF40 A1 BK 40% Glass Filled
- Lubrizol Estane® ZHF 95AT3 Thermoplastic Polyurethane, Flame Retardant
- DuPont 20 Series 2020T Specialty Polyethylene Resin
- A. Schulman POLYBATCH™ White 8153/UV2 Concentrate Based In Polyethylene
- CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Rolled Copper Alloy
- 3M Scotch-Weld™ DP604NS Structural Adhesive
- SABIC Innovative Plastics LNP Thermotuf PF003IX1 PA 6 (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved