Kingfa JE2-R2G30 Glass Fiber Reinforced ABS/PBT Alloy

Category	Polymer , Thermoplastic , ABS Polymer , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	Kingfa Sci. & Tech. Co.
Trade Name
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Kingfa JE2-R2G30 Glass Fiber Reinforced ABS/PBT Alloy.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Features:High stiffness, high hardnessGood mechanical strengthGood chemical resistanceGood size stabilityGood heat stabilityLow tendency to warpApplications:Optical appliance (camera, video)Sports appliancePrinter, photocopier cabinetScanner partsAutomobile instrument panelsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.41 g/cc <br>@Temperature 23.0 °C	1.41 g/cc <br>@Temperature 73.4 °F	ASTM D792
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm <br>@Temperature 23.0 °C	0.0050 - 0.0070 in/in <br>@Temperature 73.4 °F	Plumb; ASTM D955
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm <br>@Temperature 23.0 °C	0.0020 - 0.0030 in/in <br>@Temperature 73.4 °F	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	84	84	ASTM D785
Tensile Strength at Break	112 MPa	16200 psi	10mm/min; ASTM D638
Elongation at Break	5.0 %	5.0 %	10mm/min; ASTM D638
Flexural Strength	185 MPa	26800 psi	2mm/min; ASTM D790
Flexural Modulus	9.50 GPa	1380 ksi	2mm/min; ASTM D790
Izod Impact, Notched	0.800 J/cm <br>@Thickness 3.20 mm,<br> Temperature 23.0 °C	1.50 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 73.4 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	130 °C <br>@Thickness 6.40 mm	266 °F <br>@Thickness 0.252 in	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	118 °C <br>@Thickness 6.40 mm	244 °F <br>@Thickness 0.252 in	ASTM D648
Flammability, UL94	V-2 <br>@Thickness 1.60 mm	V-2 <br>@Thickness 0.0630 in
	V-2 <br>@Thickness 3.30 mm	V-2 <br>@Thickness 0.130 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257

Processing Properties	Metric	English	Comments
Processing Temperature	<= 265 °C	<= 509 °F
Rear Barrel Temperature	245 - 265 °C	473 - 509 °F	Start Point: 250°C
Middle Barrel Temperature	240 - 260 °C	464 - 500 °F	Start Point: 245°C
Front Barrel Temperature	235 - 260 °C	455 - 500 °F	Start Point: 240°C
Melt Temperature	235 - 260 °C	455 - 500 °F	Start Point: 250°C
Mold Temperature	60.0 - 110 °C	140 - 230 °F	Start Point: 90°C
Drying Temperature	100 - 110 °C <br>@Time 7200 - 10800 sec	212 - 230 °F <br>@Time 2.00 - 3.00 hour	Pre-dry
Back Pressure	0.300 - 1.00 MPa	43.5 - 145 psi

Descriptive Properties	Value	Comments
Injection Speed	60-80%