SABIC Innovative Plastics LNP THERMOCOMP BF004 SAN
| Category | Polymer , Thermoplastic , SAN Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP BF004 SAN.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* BF004 is a compound based on SAN resin containing 20% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.190 % | 0.190 % | 50% RH, 24 hrs; ASTM D570 |
| 0.260 % | 0.260 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 103 MPa | 14900 psi | 5 mm/min; ISO 527 |
| 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.22 GPa | 1190 ksi | 1 mm/min; ISO 527 |
| 8.26 GPa | 1200 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 140 MPa | 20300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.28 GPa | 1060 ksi | 2 mm/min; ISO 178 |
| 7.59 GPa | 1100 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.96 J/cm | 3.67 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*3; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 44.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
24.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 47.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 100 °C @Thickness 3.20 mm |
212 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylac® FR74 ABS
- Petroquimica Triunfo Trithene® TU 3001 LDPE - Agricultural Film
- Gouda Vuurvast CURAS 90 PF REPAIR Moldable Refractory Material
- Kraton® D2109 DS-N (SBS) Compound
- Borealis Borcoat™ EA165E Elastomer Modified Polypropylene for Extrusion
- Westlake EF606 Low Density Polyethylene
- Dow TUFLIN™ HS-7028 NT 7 Linear Low Density Polyethylene Resin
- AK Steel ZINCGRIP® GA Hot Dip Galvannealed Carbon Commercial Steel (CS Type B), Standard Grade
- LG Chemical LG-512 Styrene-Butadiene-Styrene
Copyright © lookpolymers.com All Rights Reserved