SABIC Innovative Plastics LNP THERMOCOMP UF009AS PPA (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP UF009AS PPA (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* UF009AS is a compound based on Polyphthalamide resin containing Glass Fiber.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
on Tensile Bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 194 MPa
28100 psi
5 mm/min; ISO 527
Tensile Strength, Yield 111 MPa
16100 psi
5 mm/min; ISO 527
Elongation at Break 1.3 %
1.3 %
5 mm/min; ISO 527
Elongation at Yield 0.80 %
0.80 %
5 mm/min; ISO 527
Tensile Modulus 14.4 GPa
2090 ksi
1 mm/min; ISO 527
Flexural Strength 387 MPa
56100 psi
2 mm/min; ISO 178
Flexural Modulus 13.2 GPa
1910 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 90.0 kJ/m²
42.8 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 19.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 10.6 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 52.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 28.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2