SABIC Innovative Plastics LNP STAT-KON RE0069S PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON RE0069S PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* RE0069S is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabilized.
Physical Properties Metric English Comments
Specific Gravity 1.49 g/cc
1.49 g/cc
ASTM D792
Density 1.49 g/cc
0.0538 lb/in³
ISO 1183
1.50 g/cc
0.0542 lb/in³
ASTM D792
Moisture Absorption 0.400 %
0.400 %
50% RH, 24 hrs; ASTM D570
0.560 %
0.560 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
 0.0010 - 0.0030 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 199 MPa
28900 psi
Type I, 50 mm/min; ASTM D638
207 MPa
30000 psi
5 mm/min; ISO 527
Tensile Strength, Yield 199 MPa
28900 psi
Type I, 50 mm/min; ASTM D638
207 MPa
30000 psi
5 mm/min; ISO 527
Elongation at Break 1.4 %
1.4 %
5 mm/min; ISO 527
1.6 %
1.6 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 1.4 %
1.4 %
5 mm/min; ISO 527
1.6 %
1.6 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 24.95 GPa
3619 ksi
1 mm/min; ISO 527
26.96 GPa
3910 ksi
50 mm/min; ASTM D638
Flexural Strength 269 MPa
39000 psi
1.3 mm/min, 50 mm span; ASTM D790
324 MPa
47000 psi
ISO 178
Flexural Yield Strength 269 MPa
39000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 18.59 GPa
2696 ksi
1.3 mm/min, 50 mm span; ASTM D790
19.56 GPa
2837 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.760 J/cm
1.42 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.18 J/cm
19.07 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 34.0 kJ/m²
16.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J

@Temperature 23.0 °C
 5.90 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 8.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
 4.44 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 8.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
 4.44 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
255 °C

@Thickness 3.20 mm
 491 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
242 °C

@Thickness 3.20 mm
 468 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 1.0 - 4.0 ohm
1.0 - 4.0 ohm
ASTM D257