Polymer Property : Linear Mold Shrinkage, Flow = 0.013 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.0090 - 0.013 cm/cm	0.0090 - 0.013 in/in	ASTM D955
PolyOne Maxxam™ PPH-20C Nat Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Linear Mold Shrinkage, Flow	0.0070 - 0.013 cm/cm	0.0070 - 0.013 in/in	ASTM D955
PolyOne Versollan™ OM 1255NX-1 Thermoplastic Elastomer (TPE) Versollan™ OM 1255NX-1 is a high performance TPU alloy designed for thin-wall overmolding onto polycarbonate (PC), ABS, PC/ABS and copolyester substrates. - Improved Grip with Matte, Rubbery Finish..
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in	ISO 294-4
Polyplastic Armlen® PP-2FR Polypropylene, Flame Retardant Flame retardant, RoHS compliantInformation provided by PolyPlastic Group.
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in	0.125"x0.5"x5" bar; ASTM D955
Solvay Specialty Polymers KetaSpire® KT-820 Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpire PEEK is produced to the highest industry standards and is characteriz..
Linear Mold Shrinkage, Flow	0.0090 - 0.013 cm/cm @Thickness 3.20 mm	0.0090 - 0.013 in/in @Thickness 0.126 in	ASTM D955
LG Chemical LUMID GP3150A(W) PA6+MF15%, General Purpose Feature: Injection Molding, PA6+MF15%, General PurposeApplication: E&E (Rice Cooer Housing)CAS No. 25038-54-4 and 14807-96-6Information provided by LG Chemical
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm @Thickness 3.20 mm	0.011 - 0.013 in/in @Thickness 0.126 in	ASTM D955
LG Chemical LUPOL HI5204G PP+MF20%, High Impact Description: Injection Molding, PP+MF20%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 26221-73-8 and 14807-96-6Information provided by LG Chemical
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm @Thickness 3.20 mm	0.011 - 0.013 in/in @Thickness 0.126 in	ASTM D955
LG Chemical LUPOL HI5204H PP+MF20%, High Impact Description: Injection Molding, PP+MF20%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 26221-73-8 and 14807-96-6Information provided by LG Chemical
Linear Mold Shrinkage, Flow	0.0090 - 0.013 cm/cm @Thickness 3.20 mm	0.0090 - 0.013 in/in @Thickness 0.126 in	ASTM D955
LG Chemical LUPOL GP3156F Flame Retardant PP Description: Injection Molding, FR PP, General Purpose, Flame RetardantApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0, 84852-53-9, 14807-96-6 and 1309-64-4Information provided ..
Linear Mold Shrinkage, Flow	0.010 - 0.013 cm/cm	0.010 - 0.013 in/in
LATI Laticonther 52/35 CP1/45 PP Homopolymer High thermal conductivity product based on Polypropylene homopolymer (PPh). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided..
Linear Mold Shrinkage, Flow	0.0070 - 0.013 cm/cm	0.0070 - 0.013 in/in
LATI Latimass 63-06 D025 PA66 Specific density compound based on Polyamide 66 (PA66). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria T..
Linear Mold Shrinkage, Flow	0.010 - 0.013 cm/cm	0.010 - 0.013 in/in
LATI Latimass 75/4-04 D009 PA12 Specific density compound based on Polyamide 12 (PA12). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria T..
Linear Mold Shrinkage, Flow	0.0090 - 0.013 cm/cm	0.0090 - 0.013 in/in	SABIC Method
SABIC Innovative Plastics LNP LUBRICOMP RAL22 PA 66 (Europe-Africa-Middle East) LNP* LUBRICOMP* RAL22 is a compound based on PA66 resin containing PTFE, Aramid Fiber. Added Features: Internally Lubricated
Linear Mold Shrinkage, Flow	0.0090 - 0.013 cm/cm	0.0090 - 0.013 in/in	SABIC Method
SABIC Innovative Plastics LNP LUBRICOMP RAL23S PA 66 (Europe-Africa-Middle East) LNP LUBRICOMP* RAL23S is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber. Added features of this material include: Heat Stabilized.
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in
Solvay Specialty Polymers KetaSpireÂ® KT-851 NL Polyetheretherketone (PEEK) KetaSpireÂ® KT-851 NL resin is a depth-filtered grade of polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form and is specially designed for use in extruded wire insula..
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in
Solvay Specialty Polymers KetaSpireÂ® KT-XXXX Polyetheretherketone (PEEK) KetaSpireÂ® KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpireÂ® PEEK is produced to the highest industry standards and is cha..
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in	ASTM D955
Shinkong Synthetic Fibers ShiniteÂ® D201M20 PBT, 20% Mineral Filled Information from Shinkong Synthetic Fibers Corp.
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm @Thickness 3.20 mm	0.011 - 0.013 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics NORYL GTX GTX910 PPE+PS+PA Unfilled grade for automotive on-line painted components. Dimensional stability. Excellent chemical resistance. Class A surface appearance.
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm @Thickness 3.20 mm	0.011 - 0.013 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics NORYL GTX GTX910 PPE+PS+PA (Asia Pacific) Unfilled grade for automotive on-line painted components. Dimensional stability. Excellent chemical resistance. Class A surface appearance.
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in	on Tensile Bar; SABIC Method
SABIC Innovative Plastics NORYL GTX GTX975 PPE+PA (Europe-Africa-Middle East) NORYL GTX975 is a 18% mineral filled material especially designed for in- or on-line painted exterior automotive trim part, e.g. tankflaps and corner panels. This material combines high stiffness an..
Linear Mold Shrinkage, Flow	0.010 - 0.013 cm/cm @Thickness 3.20 mm	0.010 - 0.013 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics Noryl GTX GTX977 PPE+PA66 Noryl GTX GTX977 resin is a mineral reinforced conductive Noryl GTX with a improved CTE (7) with a balanced performance of Impact and stiffness. (developmental grade : EXNX0074)This data was supplie..
Linear Mold Shrinkage, Flow	0.010 - 0.013 cm/cm @Thickness 3.20 mm	0.010 - 0.013 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics Noryl GTX GTX977 PPE+PA66 (Asia Pacific) Noryl GTX GTX977 resin is a mineral reinforced conductive Noryl GTX with a improved CTE (7) with a balanced performance of Impact and stiffness. (developmental grade : EXNX0074)This data was supplie..
Linear Mold Shrinkage, Flow	0.0070 - 0.013 cm/cm	0.0070 - 0.013 in/in	on Tensile Bar; SABIC Method
SABIC Innovative Plastics ValoxÂ® SHF4910 PBT (Europe-Africa-Middle East) 6.5% glass reinforced, Super High Flow, flame retardant PBT.
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in	ASTM D955
Shinkong Synthetic Fibers ShiniteÂ® D201M20 PBT, 20% Mineral Filled Information from Shinkong Synthetic Fibers Corp.
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm @Thickness 3.20 mm	0.011 - 0.013 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics NORYL GTX GTX6011 PPE+PA6 (Asia Pacific) PA6 based unfilled GTX. High impact.
Linear Mold Shrinkage, Flow	0.010 - 0.013 cm/cm @Thickness 3.20 mm	0.010 - 0.013 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics NORYL GTX GTX674PC PPE+PA6 A conductive PPE/PA blend designed to have improved surface appearance and elevated heat resistance for powder coating. The material is suitable for injection molding. The material is only availab..
Linear Mold Shrinkage, Flow	0.0090 - 0.013 cm/cm	0.0090 - 0.013 in/in	ASTM D955
Chase Plastics CP Pryme® N100HL (Dry) Nylon 6, Heat Stabilized, Lubricated Features: Heat stabilizedLubricatedForm: PelletsInformation provided by Chase Plastics.
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm	0.011 - 0.013 in/in	ISO DIS 294-4
Wellman Wellamid® NY1599-GY Unfilled Nylon 66 Description: Unfilled Nylon 66Information provided by Wellman.
Linear Mold Shrinkage, Flow	0.011 - 0.013 cm/cm @Thickness 4.00 mm	0.011 - 0.013 in/in @Thickness 0.157 in	E2P method
Eurostar Staramide 6 80E10 PA6, Injection Molded Staramide 6 80E10 is a high density, Polyamide 6, Injection Molding Resin (also known as 680E10)Information provided by Eurostar.
Linear Mold Shrinkage, Flow	0.0090 - 0.013 cm/cm	0.0090 - 0.013 in/in	on Tensile Bar; E2P method
Eurostar Staramide AK8 PA66, 40% Mineral Reinforced, Injection Molding Staramide AK8 is a 40% Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Linear Mold Shrinkage, Flow	0.0105 - 0.013 cm/cm	0.0105 - 0.013 in/in
LATI Latilub 95-15T PSU, PTFE Filled Self-lubricating product based on Polysulfone (PSU). PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici ..