LATI Latimass 63-06 D025 PA66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer	LATI
Trade Name	Latimass
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latimass 63-06 D025 PA66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Specific density compound based on Polyamide 66 (PA66). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	2.70 g/cc	0.0975 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0070 - 0.013 cm/cm	0.0070 - 0.013 in/in
Linear Mold Shrinkage, Transverse	0.0070 - 0.013 cm/cm	0.0070 - 0.013 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	15.0 MPa	2180 psi
Elongation at Break	7.0 %	7.0 %
Tensile Modulus	1.90 GPa	276 ksi
Charpy Impact Unnotched	3.00 J/cmÂ²	14.3 ft-lb/inÂ²
Charpy Impact, Notched	0.300 J/cmÂ²	1.43 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	195 Â°C	383 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	145 Â°C	293 Â°F
Vicat Softening Point	145 Â°C @Load 5.00 kg	293 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	240 - 260 Â°C	464 - 500 Â°F
Mold Temperature	60.0 - 80.0 Â°C	140 - 176 Â°F
Drying Temperature	80.0 - 100 Â°C @Time 10800 sec	176 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa