Eurostar Staramide AK8 PA66, 40% Mineral Reinforced, Injection Molding

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide AK8 PA66, 40% Mineral Reinforced, Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Staramide AK8 is a 40% Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
Moisture Absorption 0.0900 %

@Temperature 23.0 °C
 0.0900 %

@Temperature 73.4 °F
 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0090 - 0.013 cm/cm
0.0090 - 0.013 in/in
on Tensile Bar; E2P method
Mechanical Properties Metric English Comments
Hardness, Rockwell L 92
92
ISO 2039-2
Tensile Strength at Break 75.0 MPa
10900 psi
5 mm/min; ISO 527
Elongation at Break 10 %
10 %
5 mm/min; ISO 527
Tensile Modulus 5.20 GPa
754 ksi
1 mm/min; ISO 527
Flexural Strength 135 MPa
19600 psi
2 mm/min; ISO 178
Flexural Modulus 5.20 GPa
754 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 80x10x4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 80x10x4; ISO 180/1A
Charpy Impact Unnotched >= 10.0 J/cm²

@Temperature 23.0 °C
 >= 47.6 ft-lb/in²

@Temperature 73.4 °F
 Edgew 80x10x4 sp=62; ISO 179/1eU
>= 10.0 J/cm²

@Temperature -30.0 °C
 >= 47.6 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80x10x4 sp=62; ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80x10x4 sp=62; ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 Edgew 80x10x4 sp=62; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 33.3 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 33.3 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Hot Ball Pressure Test 123 - 127 °C
253 - 261 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 231 °C
448 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point 251 °C
484 °F
B/120; ISO 306
252 °C
486 °F
B/50; ISO 306
Flame Spread 2.00 mm/min

@Thickness 2.00 mm
 0.0787 in/min

@Thickness 0.0787 in
 FMVSS Burning Speed
6.00 mm/min

@Thickness 2.00 mm
 0.236 in/min

@Thickness 0.0787 in
 FMVSS Burning Speed
Oxygen Index 32 %
32 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Dielectric Strength 18.0 kV/mm

@Thickness 3.20 mm
 457 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Processing Properties Metric English Comments
Zone 1 260 - 280 °C
500 - 536 °F
Zone 2 270 - 280 °C
518 - 536 °F
Zone 3 270 - 290 °C
518 - 554 °F
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 75.0 - 85.0 °C

@Time 14400 - 21600 sec
 167 - 185 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %