SABIC Innovative Plastics NORYL GTX GTX674PC PPE+PA6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX674PC PPE+PA6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A conductive PPE/PA blend designed to have improved surface appearance and elevated heat resistance for powder coating. The material is suitable for injection molding. The material is only available in black.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.013 cm/cm @Thickness 3.20 mm |
0.010 - 0.013 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 25 g/10 min @Load 5.00 kg, Temperature 300 °C |
25 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 50 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.81 GPa | 408 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 103 MPa | 14900 psi | 2 mm/min; ISO 178 |
| 109 MPa | 15800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.48 GPa | 360 ksi | 2 mm/min; ISO 178 |
| 2.89 GPa | 419 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| 0.500 J/cm @Temperature -30.0 °C |
0.937 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 76.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 81.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
45.0 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 78.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 86.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.8 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 188 °C @Thickness 3.20 mm |
370 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 196 °C | 385 °F | Rate B/120; ISO 306 |
| 197 °C | 387 °F | Rate B/50; ASTM D1525 | |
| 197 °C | 387 °F | Rate B/50; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 - 10000 ohm-cm | 1000 - 10000 ohm-cm | SABIC Method |
Users viewing this material also viewed the following:
- Flint Hills 44S2A Polypropylene Impact Copolymer
- Hyosung Topilene R401 PP
- LG Chemical LUMILOY GN1006F Injection Molding FR mPPO
- Gouda Vuurvast VIBRON 160 K 50 Dense Vibrating Refractory Castable
- Lanxess Durethan® BKY 115 H3.0 DUS008 Nylon 6, 15% Glass Fiber
- A. Schulman POLYBATCH™ Treated Pine 60175U/4 Concentrate Based In LLDPE
- A. Schulman POLYBATCH™ Green 30394 Concentrate Based In LDPE
- ExxonMobil SpectraSyn Plus™ 4 Advanced Polyalphaolefin (PAO) Fluid
- Dow Saran® 560 Clear Plastic Barrier Film
- Aremco Ceramabind™ 880 High Temperature Inorganic Binder
Copyright © lookpolymers.com All Rights Reserved