SABIC Innovative Plastics NORYL GTX GTX975 PPE+PA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX975 PPE+PA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NORYL GTX975 is a 18% mineral filled material especially designed for in- or on-line painted exterior automotive trim part, e.g. tankflaps and corner panels. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting in an unique way.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.013 cm/cm | 0.011 - 0.013 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 280 °C |
10 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 125 MPa | 18100 psi | ISO 2039-1 |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.20 GPa | 609 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.00 GPa | 580 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| 35.0 kJ/m² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Vicat Softening Point | 195 °C | 383 °F | Rate B/50; ISO 306 |
| 200 °C | 392 °F | Rate B/120; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 - 10000 ohm-cm | 1000 - 10000 ohm-cm | SABIC Method |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG47 ABS (Asia Pacific)
- Overview of materials for Acetal Copolymer, Aramid Fiber Filled
- Kinlead LSS11 Low Temperature Grade Heat Sealable Film (thickness: 20 µm)
- Lanxess Pocan® KU 1-7313 000000 PBT + PET, 15% Glass Fiber
- Eagle Brass 200/201 Nickel Alloy, Annealed
- CENTROPLAST CENTROPHEN GF Polyphenylene ether 30% glass fiber
- Axiall 22950 Coax & Telecom Flexible PVC
- Polimeri Europa Europrene® SOL T 161B Styrene - Butadiene Block Copolymer
- Ravago Manufacturing Americas Hylex® P1010G15 HB Polycarbonate, 15% Fiberglass Reinforced
- Hexcel® HexForce™ 7532 Fiber Glass Fabric