SABIC Innovative Plastics LNP LUBRICOMP RAL22 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RAL22 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RAL22 is a compound based on PA66 resin containing PTFE, Aramid Fiber. Added Features: Internally Lubricated
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.013 cm/cm | 0.0090 - 0.013 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 8.4 % | 8.4 % | Flexural Strain, break, 2 mm/min; ISO 178 |
| Elongation at Yield | 7.4 % | 7.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.60 GPa | 522 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 106 MPa | 15400 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 109 MPa | 15800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.40 GPa | 493 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.54 | 0.54 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.45 | 0.45 | ASTM D3702 Modified |
| K (wear) Factor | 26.2 x 10-8 mm³/N-M | 13.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Mistron Vapor Filler
- Albis Plastics Tedur® L V 9112-2 PPS, 20% Glass Fiber (discontinued **)
- Lehmann & Voss LUVOCOM® 65-8285 PP-copolymer, with carbon fiber
- LATI Later 4 K/30 PBT, 30% Carbon Fiber Reinforced
- SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66
- Formosa Plastics Formolene® 2610A Compounding and Injection Molding Polypropylene
- Total PPC M6823MZ Metallocene Isostatic Propylene Polymer
- Diamond Polymers ASA S319
- Braskem IG58 HDPE Injection Molding Polyethylene Copolymer
Copyright © lookpolymers.com All Rights Reserved