LATI Latimass 75/4-04 D009 PA12

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	LATI
Trade Name	Latimass
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latimass 75/4-04 D009 PA12.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Specific density compound based on Polyamide 12 (PA12). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.00 g/cc	0.0361 lb/inÂ³
Linear Mold Shrinkage, Flow	0.010 - 0.013 cm/cm	0.010 - 0.013 in/in
Linear Mold Shrinkage, Transverse	0.0090 - 0.012 cm/cm	0.0090 - 0.012 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	25.0 MPa	3630 psi
Elongation at Break	0.70 %	0.70 %
Tensile Modulus	3.40 GPa	493 ksi
Charpy Impact Unnotched	1.00 J/cmÂ²	4.76 ft-lb/inÂ²
Charpy Impact, Notched	0.120 J/cmÂ²	0.571 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	165 Â°C	329 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	70.0 Â°C	158 Â°F
Vicat Softening Point	180 Â°C @Load 5.00 kg	356 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	230 - 250 Â°C	446 - 482 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	120 - 130 Â°C @Time 10800 sec	248 - 266 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa