Category Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name NORYL GTX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL GTX GTX910 PPE+PS+PA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unfilled grade for automotive on-line painted components. Dimensional stability. Excellent chemical resistance. Class A surface appearance.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Density 1.107 g/cc
0.03999 lb/in³
ASTM D792
Moisture Absorption 0.500 %
0.500 %
50% RH, 24 hrs; ASTM D570
Moisture Absorption at Equilibrium 1.0 %
1.0 %
50% RH; ASTM D570
Linear Mold Shrinkage, Flow 0.016 - 0.018 cm/cm
0.016 - 0.018 in/in
annealed 130C 1hr; ASTM D955
0.011 - 0.013 cm/cm

@Thickness 3.20 mm
 0.011 - 0.013 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Thickness 3.20 mm
 0.010 - 0.012 in/in

@Thickness 0.126 in
 SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell R 116
116
ASTM D785
Tensile Strength at Break 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 60 %
60 %
Type I, 50 mm/min; ASTM D638
Flexural Yield Strength 95.0 MPa
13800 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 2.24 GPa
325 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 2.40 J/cm
4.50 ft-lb/in
ASTM D256
1.33 J/cm

@Temperature -30.0 °C
 2.49 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Dart Drop, Total Energy 50.0 J
36.9 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
39.0 J

@Temperature -30.0 °C
 28.8 ft-lb

@Temperature -22.0 °F
 Instrumented Impact Energy @ peak; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
126 µm/m-°C

@Temperature 60.0 - 138 °C
 70.0 µin/in-°F

@Temperature 140 - 280 °F
 ASTM E 831
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
126 µm/m-°C

@Temperature 60.0 - 138 °C
 70.0 µin/in-°F

@Temperature 140 - 280 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 193 °C

@Thickness 6.40 mm
 379 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 143 °C

@Thickness 6.40 mm
 289 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 232 °C
450 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.49 mm
 HB

@Thickness 0.0587 in
 UL 94
Electrical Properties Metric English Comments
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
Tungsten; ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A