- Polymer Property : Linear Mold Shrinkage, Flow = 0.0025 cm/cm
Polymer Property : Linear Mold Shrinkage, Flow = 0.0025 cm/cm Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0025 cm/cm | 0.00050 - 0.0025 in/in | |
| LATI Larpeek 10 K/30 PEEK, 30% Carbon Fiber Reinforced Polyetheretherketone (PEEK) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As.. |
|||
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0025 cm/cm | 0.00050 - 0.0025 in/in | |
| LATI Larpeek 50 K/30 PEEK, 30% Carbon Fiber Reinforced Polyetheretherketone (PEEK) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As.. |
|||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm | 0.0010 - 0.0025 in/in | |
| LATI Larton GCE/600 PPS, Glass/Mineral Reinforced Polyphenylene Sulfide (PPS) based compound. Glass fibers / Mineral filler. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa .. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm | 0.0015 - 0.0025 in/in | |
| LATI Latilub 87/28-15T K/20 PC, 20% Carbon Fiber Reinforced, PTFE Filled Self-lubricating product based on Polycarbonate (PC). PTFE. Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria.. |
|||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm | 0.0010 - 0.0025 in/in | |
| LATI Latiohm 85-06 PD01 G/15 PES, 15% Glass Fiber Reinforced Semiconductive/dissipative product based on Polyether Sulfone (PES). Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I.. |
|||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics NORYL ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1520A PC LNP* Lubricomp* Lexan_LF1520A compound is a 20% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0025 cm/cm @Thickness 3.20 mm |
0.00050 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1530A PC LNP* Lubricomp* Lexan_LF1530A compound is a 30% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics LNP LUBRICOMP Noryl_NF1520 PPE+HIPS (Europe-Africa-Middle East) LNP* Lubricomp* Noryl_NF1520 compound is a 20% glass reinforced, 15% PTFE. Wear resistant; 211F HDT @ 264 psi. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics Ultem 3451 PEI 45% Glass fiber and mineral filled, standard flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming.This data was supplied by SABIC-IP for the Americas region. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics Ultem 3451 PEI (Asia Pacific) 45% Glass fiber and mineral filled, standard flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics ULTEM 3452 PEI 45% Glass fiber and mineral filled, enhanced flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming, UL94 V0 and 5VA listing in recognized colors. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics ULTEM 3452 PEI (Asia Pacific) 45% Glass fiber and mineral filled, enhanced flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming, UL94 V0 and 5VA listing in recognized colors. |
|||
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0025 cm/cm | 0.00050 - 0.0025 in/in | on tensile bar; SABIC Method |
| SABIC Innovative Plastics LNP Stat-kon OCL13 PPS - LINEAR (Europe-Africa-Middle East) LNP* Stat-kon* OCL13 is a compound based on PPS - LINEAR resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for.. |
|||
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0025 cm/cm | 0.00050 - 0.0025 in/in | on Tensile Bar; SABIC Method |
| SABIC Innovative Plastics LNP STAT-KON OE008A PPS - Branched (Europe-Africa-Middle East) LNP* Stat-kon* OC-1008 is a compound based on PPS - Branched resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics Xenoy® X2420 PC+POLYESTER (Asia Pacific) Xenoy*X2420 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and impact strength. X2420 has enhanced melt flowability, impact ductility and broad co.. |
|||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm @Time 86400 sec |
0.0010 - 0.0025 in/in @Time 24.0 hour |
ASTM D955 |
| SABIC Innovative Plastics LNP THERMOCOMP EXTC8141 PC (Asia Pacific) LNP* Thermocomp* EXTC8141 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, No.. |
|||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK500 PC+ABS LNP* Thermocomp* Lexan_JK500 compound is a 10% GR, ECO conforming FR, PC+ABS for thinwall molding applications. |
|||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK500 PC+ABS (Asia Pacific) 10% GR, ECO conforming FR, PC+ABS for thinwall molding applications. |
|||
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0025 cm/cm @Thickness 3.20 mm |
0.00050 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC LNP* Thermocomp* Lexan_LGN5030 compound is a glass reinforced. Flame retardant. |
|||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics NORYL GTX GTX8730 PPE+PA Noryl GTX* GTX8730 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-s.. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics NORYL HM4025H PPE+PS (Asia Pacific) 40% GF/MF filled FR PPE/PS blend, high flow |
|||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Europe-Africa-Middle East) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm | 0.0010 - 0.0025 in/in | on Tensile Bar; ISO 294 |
| Eurostar Staramide AG10K PA66, 50% Glass Filled, Injection Molded AG10 is a Heat and Hydrolytically Stabilized, 50% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive suppl.. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm | 0.0015 - 0.0025 in/in | on Tensile Bar; E2P method |
| Eurostar Staramide BG8 PA6, 40% Glass Fiber Filled, Injection Molded Staramide BG8 is a 40% Glass Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar. |
|||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm | 0.0010 - 0.0025 in/in | on Tensile Bar; E2P method |
| Eurostar Staramide RF00AES PA66/6, 50% Glass Filled, Injection Molded Staramide RF00AES is a 50% Glass Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as Staramide 66 C 50V S3)Information provided by Eurostar. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics LNP STAT-KON Noryl_FMC1010 PPE+HIPS (Europe-Africa-Middle East) LNP* Stat-kon* Noryl_FMC1010 compound is a 10% carbon fiber, static dissipative, foamable resin Nonchlorinated, nonbrominated. UL94 V1 rated. Property values at 20% WR, 0.250"" wall. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGN2000A PC (Europe-Africa-Middle East) LNP* Thermocomp* Lexan_LGN2000A compound is a 20% glass reinforced PC, high flow. UL rated V-0. Consumer Electronics applications. |
|||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics NORYL CN5260 PPE+PS (Asia Pacific) 50% filled FR high modulus PPE/PS blend |
|||
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0025 cm/cm @Thickness 3.20 mm |
0.00050 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC (Asia Pacific) Glass reinforced. Flame retardant. |
|||