Eurostar Staramide BG8 PA6, 40% Glass Fiber Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide BG8 PA6, 40% Glass Fiber Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Staramide BG8 is a 40% Glass Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0015 - 0.0025 cm/cm
0.0015 - 0.0025 in/in
on Tensile Bar; E2P method
Mechanical Properties Metric English Comments
Tensile Strength at Break 195 MPa
28300 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 13.5 GPa
1960 ksi
1 mm/min; ISO 527
Flexural Strength 290 MPa
42100 psi
2 mm/min; ISO 178
Flexural Modulus 12.0 GPa
1740 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 15.0 kJ/m²

@Temperature -40.0 °C
 7.14 ft-lb/in²

@Temperature -40.0 °F
 80x10x4; ISO 180/1A
16.0 kJ/m²

@Temperature -20.0 °C
 7.61 ft-lb/in²

@Temperature -4.00 °F
 80x10x4; ISO 180/1A
17.0 kJ/m²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 80x10x4; ISO 180/1A
Charpy Impact Unnotched 15.0 J/cm²
71.4 ft-lb/in²
Edgew 80x10x4 sp=62; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 17.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 9.44 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 82.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 45.6 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Thermal Conductivity 0.330 W/m-K
2.29 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 212 °C
414 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point 220 °C
428 °F
B/120; ISO 306
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
Oxygen Index 25 %
25 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
 3.4

@Frequency 1.00e+6 Hz
 IEC 60250
3.6

@Frequency 50.0 - 60.0 Hz
 3.6

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 20.0 kV/mm

@Thickness 3.20 mm
 508 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Dissipation Factor 0.0061

@Frequency 50.0 - 60.0 Hz
 0.0061

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.016

@Frequency 1.00e+6 Hz
 0.016

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 350 V
350 V
M; IEC 60112
500 V
500 V
IEC 60112
Processing Properties Metric English Comments
Zone 1 230 - 240 °C
446 - 464 °F
Zone 2 240 - 250 °C
464 - 482 °F
Zone 3 240 - 270 °C
464 - 518 °F
Melt Temperature 240 - 270 °C
464 - 518 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 75.0 - 85.0 °C

@Time 14400 - 21600 sec
 167 - 185 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %