SABIC Innovative Plastics ULTEM 3452 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 3452 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
45% Glass fiber and mineral filled, enhanced flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.66 g/cc | 1.66 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 4.6 g/10 min @Load 6.60 kg, Temperature 337 °C |
4.6 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.4 % | 1.4 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 179 MPa | 26000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 12.41 GPa | 1800 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| 2.18 J/cm @Thickness 3.20 mm |
4.08 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C @Thickness 6.40 mm |
414 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 180 °C | 356 °F | UL 746B |
| UL RTI, Mechanical with Impact | 180 °C | 356 °F | UL 746B |
| UL RTI, Mechanical without Impact | 180 °C | 356 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.780 mm |
V-0 @Thickness 0.0307 in |
UL 94 |
| 5VA @Thickness 2.99 mm |
5VA @Thickness 0.118 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Resin Technology Group CT-523LV Cationic UV Cure Epoxy Adhesive
- A. Schulman POLYBLAK™ 4669 Premium Conductive 35% Carbon Black Concentrate Based In LLDPE
- Trelleborg Emerson & Cuming Stycast® 1090/11 Two-Component General Purpose Encapsulant
- A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
- Axiall 8258 Rigid PVC, Extrusion
- 3M 5010 Polyurethane Multi-Purpose Adhesive
- Borealis Xmod™ K65G3 30% Glass Fiber Reinforced Polypropylene Compound
- Solvay ABEX® EP 120 Surfactant
Copyright © lookpolymers.com All Rights Reserved