SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGN2000A PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGN2000A PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* Lexan_LGN2000A compound is a 20% glass reinforced PC, high flow. UL rated V-0. Consumer Electronics applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0025 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 20.7 g/10 min @Load 1.20 kg, Temperature 300 °C |
20.7 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 81.0 MPa | 11700 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 4.9 % | 4.9 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.03 GPa | 730 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.00 J/cm | 7.49 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 14.0 J @Temperature 23.0 °C |
10.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 25.2 µm/m-°C @Temperature -40.0 - 95.0 °C |
14.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 48.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 55.8 µm/m-°C @Temperature -40.0 - 95.0 °C |
31.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 143 °C | 289 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.49 mm |
V-0 @Thickness 0.0587 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Network Polymers Nylon 6001 L
- Nilit FRIANYL A63 CV-CM 0830 9005/Z Powder-coatable nylon 6.6 for injection molding, 8% carbon fiber reinforced, 30% ceramic filled
- SABIC Innovative Plastics Xenoy® 6370 PBT+PC
- Dow Corning SYL-OFF® PMCPSL 50 Release Modifier
- DuPont™ Bynel® 41E762 Anhydride Modified LLDPE
- 3M 8777 Sealing Tape
- A. Schulman POLYBATCH™ Grey 8035 Concentrate Based In Polyethylene
Copyright © lookpolymers.com All Rights Reserved