SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* Lexan_LGN5030 compound is a glass reinforced. Flame retardant.
Physical Properties Metric English Comments
Specific Gravity 1.61 g/cc
1.61 g/cc
ASTM D792
Water Absorption 0.14 %

@Time 86400 sec
 0.14 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.00050 - 0.0025 cm/cm

@Thickness 3.20 mm
 0.00050 - 0.0025 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
 0.0010 - 0.0030 in/in

@Thickness 0.126 in
 SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 142 MPa
20600 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
Flexural Strength 186 MPa
27000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 10.7 GPa
1550 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.22 J/cm
2.29 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.6 µm/m-°C

@Temperature -30.0 - 30.0 °C
 12.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 39.6 µm/m-°C

@Temperature -30.0 - 30.0 °C
 22.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 143 °C

@Thickness 6.40 mm
 289 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Flammability, UL94 V-1

@Thickness 1.47 mm
 V-1

@Thickness 0.0579 in
 UL 94
V-0

@Thickness 2.79 mm
 V-0

@Thickness 0.110 in
 UL 94
5VA

@Thickness 3.60 mm
 5VA

@Thickness 0.142 in
 UL 94
Electrical Properties Metric English Comments
Dielectric Strength 16.3 kV/mm

@Thickness 3.20 mm
 414 kV/in

@Thickness 0.126 in
 in oil; ASTM D149