SABIC Innovative Plastics NORYL GTX GTX8730 PPE+PA
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX8730 PPE+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl GTX* GTX8730 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-statically painted or powder coated without the need for a conductive primer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.20 % | 1.20 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.0 % | 4.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0065 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0065 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 13.7 g/10 min @Load 5.00 kg, Temperature 280 °C |
13.7 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 280 °C |
10 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 185 MPa | 26800 psi | Type I, 5 mm/min; ASTM D638 |
| 185 MPa | 26800 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 185 MPa | 26800 psi | Type I, 5 mm/min; ASTM D638 |
| 185 MPa | 26800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 12.0 GPa | 1740 ksi | 5 mm/min; ASTM D638 |
| 12.0 GPa | 1740 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 270 MPa | 39200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 270 MPa | 39200 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 9.30 GPa | 1350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.30 GPa | 1350 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| 0.680 J/cm @Temperature -30.0 °C |
1.27 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 11.0 J/cm | 20.6 ft-lb/in | ASTM D4812 |
| 9.50 J/cm @Temperature -30.0 °C |
17.8 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 26.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 78.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 78.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 210 °C | 410 °F | Rate B/50; ASTM D1525 |
| 210 °C | 410 °F | Rate B/50; ISO 306 | |
| 210 °C | 410 °F | Rate B/120; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 500 - 10000 ohm-cm | 500 - 10000 ohm-cm | SABIC Method |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 50/TF/15/BK-1 Polycarbonate, with PTFE, easy flowing
- LG Chemical LUPOL TE-5006K Thermoplastic Elastomer Alloy, Weather Resistant
- SABIC Innovative Plastics NORYL WCP821U PPE-TPE (Asia Pacific)
- SABIC Innovative Plastics NORYL N190 PPE+HIPS (Asia Pacific)
- UBE P7115U Electronic Grade Nylon Copolymer Powder
- ExxonMobil 412 Mobilgard 12 Series
- Cresset Powers Cress-Alon™ A2350 2.35 r.v. Injection Molding Grade Nylon 6, Dry As Molded
- Asahi Glass AFLAS® 150E TFE/P Fluoroelastomer
- 3M Scotch-Weld™ DP405 LH Epoxy Adhesive
- Solvay Specialty Polymers AvaSpire® AV-651 Polyaryletherketone (PAEK) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved