SABIC Innovative Plastics LNP THERMOCOMP EXTC8141 PC (Asia Pacific)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP THERMOCOMP EXTC8141 PC (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Thermocomp* EXTC8141 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, Non-Brominated & Non-Chlorinated Flame Retardant.

Physical Properties	Metric	English	Comments
Density	1.52 g/cc	0.0549 lb/inÂ³	ASTM D792
Linear Mold Shrinkage, Flow	0.0010 - 0.0025 cm/cm @Time 86400 sec	0.0010 - 0.0025 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0010 - 0.0025 cm/cm @Time 86400 sec	0.0010 - 0.0025 in/in @Time 24.0 hour	ASTM D955
Melt Index of Compound	11 g/10 min @Load 2.16 kg, Temperature 300 Â°C	11 g/10 min @Load 4.76 lb, Temperature 572 Â°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	143 MPa	20700 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	2.3 %	2.3 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	11.72 GPa	1700 ksi	5 mm/min; ASTM D638
Flexural Strength	186 MPa	27000 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	9.75 GPa	1410 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	1.40 J/cm	2.62 ft-lb/in	ASTM D256
Izod Impact, Unnotched	5.21 J/cm	9.76 ft-lb/in	ASTM D4812
Charpy Impact Unnotched	3.30 J/cmÂ²	15.7 ft-lb/inÂ²	Edgew 80104 sp=62mm; ISO 179/1eU
Charpy Impact, Notched	1.30 J/cmÂ²	6.19 ft-lb/inÂ²	Edgew 80104 sp=62mm; ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	114 Â°C @Thickness 3.20 mm	237 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in	UL 94