LATI Larpeek 10 K/30 PEEK, 30% Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer LATI
Trade Name Larpeek
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larpeek 10 K/30 PEEK, 30% Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyetheretherketone (PEEK) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
Linear Mold Shrinkage, Flow 0.00050 - 0.0025 cm/cm
0.00050 - 0.0025 in/in
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 190 MPa

@Temperature 150 °C
 27600 psi

@Temperature 302 °F
215 MPa

@Temperature 120 °C
 31200 psi

@Temperature 248 °F
225 MPa

@Temperature 90.0 °C
 32600 psi

@Temperature 194 °F
235 MPa

@Temperature 60.0 °C
 34100 psi

@Temperature 140 °F
240 MPa

@Temperature 23.0 °C
 34800 psi

@Temperature 73.4 °F
Elongation at Break 1.3 %

@Temperature 23.0 °C
 1.3 %

@Temperature 73.4 °F
1.3 %

@Temperature 60.0 °C
 1.3 %

@Temperature 140 °F
1.3 %

@Temperature 90.0 °C
 1.3 %

@Temperature 194 °F
1.4 %

@Temperature 120 °C
 1.4 %

@Temperature 248 °F
1.4 %

@Temperature 150 °C
 1.4 %

@Temperature 302 °F
Tensile Modulus 22.6 GPa

@Temperature 150 °C
 3280 ksi

@Temperature 302 °F
23.1 GPa

@Temperature 120 °C
 3350 ksi

@Temperature 248 °F
23.5 GPa

@Temperature 90.0 °C
 3410 ksi

@Temperature 194 °F
23.7 GPa

@Temperature 60.0 °C
 3440 ksi

@Temperature 140 °F
24.0 GPa

@Temperature 23.0 °C
 3480 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 230 °C
446 °F
Deflection Temperature at 0.46 MPa (66 psi) >= 300 °C
>= 572 °F
Deflection Temperature at 1.8 MPa (264 psi) >= 300 °C
>= 572 °F
Vicat Softening Point >= 300 °C

@Load 5.00 kg
 >= 572 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Volume Resistivity 6000 ohm-cm
6000 ohm-cm
Surface Resistance 300 ohm
300 ohm
Processing Properties Metric English Comments
Melt Temperature 370 - 400 °C
698 - 752 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 - 150 °C

@Time 10800 sec
 248 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: