LATI Latilub 87/28-15T K/20 PC, 20% Carbon Fiber Reinforced, PTFE Filled

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon + PTFE Filled
Manufacturer	LATI
Trade Name	Latilub
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 87/28-15T K/20 PC, 20% Carbon Fiber Reinforced, PTFE Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polycarbonate (PC). PTFE. Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.37 g/cc	0.0495 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0015 - 0.0025 cm/cm	0.0015 - 0.0025 in/in
Linear Mold Shrinkage, Transverse	0.0025 - 0.0040 cm/cm	0.0025 - 0.0040 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	130 MPa	18900 psi
Elongation at Break	1.5 %	1.5 %
Tensile Modulus	15.3 GPa	2220 ksi
Charpy Impact Unnotched	3.00 J/cmÂ²	14.3 ft-lb/inÂ²
Charpy Impact, Notched	0.800 J/cmÂ²	3.81 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.17	0.17
Coefficient of Friction, Static	0.24	0.24
K (wear) Factor	9.00 x 10^-8 mmÂ³/N-M	4.47 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	145 Â°C	293 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	140 Â°C	284 Â°F
Vicat Softening Point	150 Â°C @Load 5.00 kg	302 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	275 - 320 Â°C	527 - 608 Â°F
Mold Temperature	80.0 - 110 Â°C	176 - 230 Â°F
Drying Temperature	110 - 130 Â°C @Time 10800 sec	230 - 266 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa