LATI Latiohm 85-06 PD01 G/15 PES, 15% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 20%Glass Fiber Filled
Manufacturer	LATI
Trade Name	Latiohm
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latiohm 85-06 PD01 G/15 PES, 15% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Semiconductive/dissipative product based on Polyether Sulfone (PES). Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.50 g/cc	0.0542 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0010 - 0.0025 cm/cm	0.0010 - 0.0025 in/in
Linear Mold Shrinkage, Transverse	0.0025 - 0.0045 cm/cm	0.0025 - 0.0045 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	150 MPa	21800 psi
Elongation at Break	1.5 %	1.5 %
Tensile Modulus	13.8 GPa	2000 ksi
Charpy Impact Unnotched	2.50 J/cmÂ²	11.9 ft-lb/inÂ²
Charpy Impact, Notched	0.600 J/cmÂ²	2.86 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	220 Â°C	428 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	210 Â°C	410 Â°F
Vicat Softening Point	215 Â°C @Load 5.00 kg	419 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	200 ohm-cm	200 ohm-cm
Surface Resistance	200 ohm	200 ohm

Processing Properties	Metric	English
Melt Temperature	350 - 390 Â°C	662 - 734 Â°F
Mold Temperature	150 - 190 Â°C	302 - 374 Â°F
Drying Temperature	150 - 180 Â°C @Time 10800 sec	302 - 356 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa