Mytex Polymers AS171L-02US Polypropylene, 13% Talc Filled

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler
Manufacturer	Mytex Polymers
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Mytex Polymers AS171L-02US Polypropylene, 13% Talc Filled.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

AS171L-02US is a compounded thermoplastic polyolefin (TPO) designed for exterior automotive applications requiring cold temperature impact, processability and paintability.This product is available in natural or generic black. Applications: Exterior parts, Body Side Moldings, Claddings. OEM Approvals: Generam Motors GMW 15185, GMP.E/P.133Data provided by Mytex Polymers

Physical Properties	Metric	English	Comments
Density	0.980 g/cc	0.0354 lb/in³	ISO 1183A
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	48 hours after molding; ISO 294-3/4
	0.0060 - 0.0080 cm/cm <br>@Temperature 80.0 °C,<br> Time 3600 sec	0.0060 - 0.0080 in/in <br>@Temperature 176 °F,<br> Time 1.00 hour	48 hours after molding; ISO 294-3/4
	0.0070 - 0.0090 cm/cm <br>@Temperature 121 °C,<br> Time 3600 sec	0.0070 - 0.0090 in/in <br>@Temperature 250 °F,<br> Time 1.00 hour	48 hours after molding; ISO 294-3/4
Melt Flow	24 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C	24 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F	ISO 1133B
Ash	13 % <br>@Temperature 950 °C	13 % <br>@Temperature 1740 °F	ISO 3451/1A

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	15.0 MPa	2180 psi	ISO 527-A/1A/50
Flexural Modulus	1.10 GPa	160 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	54.0 kJ/m² <br>@Temperature 23.0 °C	25.7 ft-lb/in² <br>@Temperature 73.4 °F	ISO 180/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F	unannealed; ISO 75-1/2