Teknor Apex Chemlon® 240 MH Nylon 6, 40% Short Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 240 MH Nylon 6, 40% Short Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Heat Stabilized; Warp Resistant Forms: Pellets Additive: Heat Stabilizer Automotive Specifications: GM GMP.PA6.011Information Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Elongation at Yield | 3.9 % | 3.9 % | ASTM D638 |
| Flexural Strength | 143 MPa | 20800 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Temperature 22.8 °C |
1.10 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.8 µm/m-°C | 31.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
|
| Oxygen Index | 23 % | 23 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 11.0 kV/mm @Thickness 3.00 mm |
280 kV/in @Thickness 0.118 in |
ASTM D149 |
| Comparative Tracking Index | 500 V | 500 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 218 - 235 °C | 425 - 455 °F | |
| Middle Barrel Temperature | 252 - 257 °C | 485 - 495 °F | |
| Front Barrel Temperature | 252 - 268 °C | 485 - 515 °F | |
| Nozzle Temperature | 252 - 268 °C | 485 - 515 °F | |
| Melt Temperature | 216 °C | 420 °F | |
| 249 - 268 °C | 480 - 515 °F | Processing Temperature | |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible R8206A Polyvinyl Chloride, Flexible (PVC, Flexible)
- Mateck GaAs
- Teknor Apex Flexalloy® 9800-55 Polyvinyl Chloride Elastomer
- ChevronTexaco 250 NC Open Gear Lubricant
- Elisto THERMOSTAR® LC 610 Insulation Material
- Technetics Group Amicon™ Acetal Copolymer (Unverified Data**)
- Huntsman PE1345 EVA Film Extrusion (discontinued **)
Copyright © lookpolymers.com All Rights Reserved