Chang Chun Plastic Longlite PM T355J Impact Phenolic Molding Compound

Category Polymer , Thermoset , Phenolic , Phenolic; Unreinforced; Molded
Manufacturer Chang Chun Plastic Co. Ltd.
Trade Name Longlite PM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chang Chun Plastic Longlite PM T355J Impact Phenolic Molding Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ASTM Grade per ASTM D700 is 13.Information provided by Dowell Trading Company Ltd.
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ASTM D792
Water Absorption 0.20 %
0.20 %
ASTM D570
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Compression; ASTM D955
0.0080 cm/cm
0.0080 in/in
Injection; ASTM D955
0.0080 cm/cm
0.0080 in/in
Transfer; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 55.0 MPa
7980 psi
ASTM D651
Flexural Yield Strength 76.0 MPa
11000 psi
ASTM D790
Compressive Yield Strength 217 MPa
31500 psi
ASTM D695
Izod Impact, Notched 0.290 J/cm
0.543 ft-lb/in
ASTM D256
Charpy Impact, Notched 0.350 J/cm²
1.67 ft-lb/in²
ASTM D256
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 190 °C
374 °F
Two Hour Heat Resistance per ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 180 °C
356 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.620 mm
 V-0

@Thickness 0.0244 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Insulation Resistance 1.00e+9 ohm
1.00e+9 ohm
After Boiling; ASTM D257
1.00e+11 ohm
1.00e+11 ohm
Normal; ASTM D257
Dielectric Strength 13.8 kV/mm
351 kV/in
ASTM D149
Arc Resistance 120 sec
120 sec
ASTM D495
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL PLC 3