SABIC Innovative Plastics LNP THERMOCOMP RF006XXY PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF006XXY PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RF006XXY is a compound based on Nylon 66 containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.640 % | 0.640 % | 50% RH, 24 hrs; ASTM D570 |
| 0.890 % | 0.890 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 183 MPa | 26500 psi | Type I, 5 mm/min; ASTM D638 |
| 183 MPa | 26500 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 180 MPa | 26100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 11.38 GPa | 1651 ksi | 5 mm/min; ASTM D638 |
| 11.61 GPa | 1684 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 275 MPa | 39900 psi | ISO 178 |
| 278 MPa | 40300 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 9.96 GPa | 1440 ksi | 2 mm/min; ISO 178 |
| 10.2 GPa | 1480 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.0 J/cm | 20.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 61.0 kJ/m² | 29.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- LyondellBasell Lupolen® 5621 D HDPE
- Techmer ES Elastoblend® PA6 GF43 IM L BKN 43% Glass Filled
- SABIC Innovative Plastics LNP LUBRICOMP ZI001 PPE+PS
- Sharadaa Ceramics REFINSUL ZAP-018 Insulating Castables
- SABIC Innovative Plastics NORYL FP3060 PPE+PS (Europe-Africa-Middle East)
- Arlon 55531R060 0.061" (1.55 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Cheng Yu Plastic A779 Lubrication ABS
- 3M Scotch® 311 Box Sealing Tape
- Fainplast Compounds CKL 63/K Flexible PVC, Sheathing Lead Free
Copyright © lookpolymers.com All Rights Reserved