Borealis FR4830 Chemically Crosslinkable Polyethylene Compound for Primary Automotive Wires

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	Borealis
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis FR4830 Chemically Crosslinkable Polyethylene Compound for Primary Automotive Wires.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

FR4830 is a chemically crosslinkable Non-halogen flame retardant Polyethylene compound for Primary Automotive and Appliance Wire. Applications: FR4830 is intended for use as a 125º C rated primary insulation for crosslinked automotive and appliance wires. Specifications FR4830 meets the applicable requirements as below when processed using sound extrusion practice and testing procedure: SAE J1128/J1127, and UL 44 SIS.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in³	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	50	50	ASTM D2240
Tensile Strength at Break	12.8 MPa	1860 psi	after aging, 168h, 165°C
	16.0 MPa	2320 psi	ASTM D412
Elongation at Break	220 %	220 %	ASTM D412

Thermal Properties	Metric	English	Comments
Brittleness Temperature	<= -50.0 °C	<= -58.0 °F	ASTM D2863
Oxygen Index	25 %	25 %	ASTM D2863

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+6 ohm-cm	>= 1.00e+6 ohm-cm	ASTM D257
Dielectric Constant	3.7 @Frequency 6.00e+7 Hz	3.7 @Frequency 6.00e+7 Hz	ASTM D150
Dielectric Strength	>= 22.0 kV/mm	>= 559 kV/in	ASTM 149
Dissipation Factor	0.010 @Frequency 6.00e+7 Hz	0.010 @Frequency 6.00e+7 Hz	ASTM D150

Processing Properties	Metric	English	Comments
Processing Temperature	55.0 °C	131 °F	humidified air drying temperature
Middle Barrel Temperature	96.0 °C	205 °F	barrel 1
	110 °C	230 °F	barrel 6
Melt Temperature	<= 125 °C	<= 257 °F

Descriptive Properties	Value	Comments
Single Vertical Flame Test	Pass	20AWG;ISO 6722/SAE J1128