SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10

Category Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Carbon Fiber Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* QCL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
1.44 g/cc
0.0520 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.19 %
0.19 %
23°C / 50% RH; ISO 62
0.13 %

@Time 86400 sec
 0.13 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ASTM D 955
0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D 955
0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 117 MPa
17000 psi
ASTM D 638
126 MPa
18300 psi
ISO 527
Elongation at Break 2.4 %
2.4 %
ISO 527
2.5 %
2.5 %
ASTM D 638
Tensile Modulus 8.82 GPa
1280 ksi
50 mm/min; ASTM D 638
9.58 GPa
1390 ksi
1 mm/min; ISO 527
Flexural Strength 171 MPa
24800 psi
ASTM D 790
185 MPa
26800 psi
ISO 178
Flexural Modulus 5.99 GPa
869 ksi
ASTM D 790
7.01 GPa
1020 ksi
ISO 178
Izod Impact, Notched 0.370 J/cm

@Temperature 23.0 °C
 0.693 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 3.79 J/cm

@Temperature 23.0 °C
 7.10 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 29.0 kJ/m²

@Temperature 23.0 °C
 13.8 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 9.00 J
6.64 ft-lb
Multiaxial Impact; ISO 6603
8.00 J

@Temperature 23.0 °C
 5.90 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Coefficient of Friction, Dynamic 0.47
0.47
ASTM D 3702 Modified
Coefficient of Friction, Static 0.37
0.37
ASTM D 3702 Modified
K (wear) Factor 127 x 10-8 mm³/N-M
63.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 193 °C
379 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
164 °C

@Thickness 3.20 mm
 327 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Volume Resistivity 1000 ohm-cm - 1e+05
1000 ohm-cm - 1e+05
ASTM D 257
Surface Resistance 1000 ohm - 1e+05
1000 ohm - 1e+05
ASTM D 257