BASF Ultraform® N2320 U035 POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultraform® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultraform® N2320 U035 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Is a POM, UV-stabilized injection-molding grade.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH; ISO 62 |
| Melt Flow | 8.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 130 MPa @Load 36.5 kg, Time 30.0 sec |
18900 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | 50 mm/min; ISO 527-2 |
| Elongation at Break | 34 % | 34 % | ISO 527-2 |
| Elongation at Yield | 12 % | 12 % | ISO 527-2 |
| Modulus of Elasticity | 2.30 GPa | 334 ksi | ISO 527-2 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 21.0 J/cm² @Temperature -30.0 °C |
99.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 25.0 J/cm² @Temperature 23.0 °C |
119 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 900 MPa | 131000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 11.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
6.11 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 |
| Melting Point | 167 °C | 333 °F | DIN 53765 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75-2 |
| Vicat Softening Point | 150 °C | 302 °F | ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 |
| 600 V | 600 V | Test solution B; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | Hopper Throat |
| Zone 1 | 205 °C | 401 °F | Feed zone |
| Zone 2 | 205 °C | 401 °F | Compression |
| Zone 3 | 210 °C | 410 °F | Metering-zone |
| Zone 4 | 210 °C | 410 °F | Nozzle |
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | Injection-molding |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Peripheral screw speed | <0.3 m/s | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Rogers Corporation Bisco™ HT-800 Cellular Silicone Foam
- Parker Chomerics CHO-SEAL® 6370 Conductive Elastomer
- Resin Technology Group Fusion 902 Odorless, Non-Frosting Fusion Cyanoacrylate
- Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work
- SABIC Innovative Plastics NORYL WCA901 PPE-TPE
- UCAR Carbon UCAR® PGX Pressure Molded Graphite
- Zhejiang Juner PP8 PP For Automotive Parts
- ATI Allvac® 718Plus™ Nickel Superalloy
- AK Steel Cold Rolled Carbon Steel, Bake Hardenable (BH 180), SAE J2340 Type 180 B
- Plaskolite West Optix® CA - 71 General Purpose Acrylic Resin
Copyright © lookpolymers.com All Rights Reserved