SABIC Innovative Plastics LNP VERTON PV007 PA 6 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON PV007 PA 6 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Verton* PV007 is a compound based on Nylon 6 resin containing Long Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | |
| Moisture Absorption | 1.30 % | 1.30 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0049 cm/cm @Time 86400 sec |
0.0049 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 190 MPa | 27600 psi | ASTM D638 |
| Tensile Strength, Yield | 190 MPa | 27600 psi | ASTM D638 |
| Elongation at Break | 2.7 % | 2.7 % | ASTM D638 |
| Elongation at Yield | 2.7 % | 2.7 % | ASTM D638 |
| Tensile Modulus | 9.65 GPa | 1400 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 296 MPa | 42900 psi | ASTM D790 |
| 297 MPa | 43100 psi | ISO 178 | |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| 9.00 GPa | 1310 ksi | ISO 178 | |
| Izod Impact, Notched | 2.13 J/cm | 3.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.41 J/cm | 27.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 86.0 kJ/m² | 40.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 7011 C Natural 70% Filler Content Polypropylene
- Polykemi AB POLYfill PP EVR8025H UV Polypropylene/EDPM, Mineral Reinforced
- Manufacturing Insight EFR-3 Enhanced Fire Retardant Additive
- Saint-Gobain COHRlastic® 3010 Low Temperature Flexibility Silicone Coated Fabric
- Saint-Gobain Chemfab® SlipGrip™ 6 PTFE/Silicone Coated Fiberglass Fabric
- SABIC Innovative Plastics ULTEM ATX200 PEI Blend (Europe-Africa-Middle East)
- DuPont Performance Polymers Zytel® 45HSB NC010 Nylon 66 (Unverified Data**)
- Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1100 (Heated 593°C)
- Adell RZ-14 Copolymer Polypropylene, 20% Calcium Carbonate Filled
- BASF Ultraform® N2644 Z9 POM + PUR
Copyright © lookpolymers.com All Rights Reserved